fly ash co 2 Catching agent preparation method and its application

A technology of fly ash and scavenger, applied in application, other household appliances, chemical instruments and methods, etc., can solve the problems of groundwater pollution, soil environment and geological structure, leakage, inability to meet and other problems

Active Publication Date: 2021-07-16
BEIJING FAIRVIEW NEW TECH CO LTD
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, GCS technology is not once and for all, due to the CO stored underground 2 Changes in the original geological structure accompanied by earthquakes, volcanic eruptions, human activities, and accumulation of supercritical pressure, or CO 2 - The long-term action of water-rock causes the rock formation to corrode and correspondingly changes the porosity and permeability coefficient of the reservoir and caprock, so leakage is likely to occur, which will have an impact on the ecological environment and human health, such as groundwater pollution , changes in soil environment and geological structure, occurrence of geological disasters, etc.; in addition, the GCS operation procedures are complicated and the processing cost is relatively high, which is more suitable for newly built thermal power plants, and the transformation cost of this technology for existing thermal power enterprises and industrial enterprises The one-time investment and new construction costs are large, which cannot meet the processing CO requirements of most enterprises. 2 requirements

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • fly ash co <sub>2</sub> Catching agent preparation method and its application
  • fly ash co <sub>2</sub> Catching agent preparation method and its application
  • fly ash co <sub>2</sub> Catching agent preparation method and its application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0066] 1. According to the proportion (mass fraction): 25% of urban sludge, 60% of fly ash, 4% of sawdust, 3% of ammonium bicarbonate, 3% of urea, and 8% of kaolin; the fly ash is ball milled and passed through a 200-mesh sieve For standby, further dry and ball mill the non-urban sludge and pass through a 200-mesh sieve for standby, mix and stir the dry powder according to the proportion and quality, mill in a ball mill for 30 minutes, then add 15% (mass fraction) of water to mix evenly, and granulate. The particle size control diameter is 4mm, the molding pressure is 12.1MPa, and the pressure is maintained for 15S; the wet granules of the sample after compression molding are first dried in an oven at (100±1)°C for 2h, and then put into a muffle furnace. Slowly raise the temperature below ℃, then gradually raise the temperature to 500℃, keep it for 30 minutes, raise the temperature to 600℃, keep it for 10 minutes, raise the temperature to 700℃, keep it for 30 minutes and then c...

Embodiment 2

[0071] 1. According to the proportion (mass fraction): 20% clay, 60% fly ash, 4% starch, 3% sodium lauryl sulfate, 3% sucrose, 10% bentonite; ball mill the fly ash to pass 200 mesh Sieve for standby, further ball mill the clay and pass through a 200-mesh sieve for standby; mix and stir the dry powder according to the proportioning quality, mill in a ball mill for 30 minutes, then add 20% (mass fraction) of water and mix evenly, granulate and shape, and the particle size is controlled to a diameter of 2mm. The molding pressure is 12.1MPa, and the pressure is maintained for 15S; the wet granules of the sample after compression molding are first dried in an oven at (100±1)°C for 2 hours, and then put into a muffle furnace, and the temperature is slowly raised below 300°C. Then gradually increase the temperature and fire to 500°C, hold for 30 minutes, heat up to 600°C, hold for 10 minutes, heat up to 700°C, hold for 10 minutes, heat up to 800°C, hold for 10 minutes, and then cool n...

Embodiment 3

[0078] 1. According to the proportioning ratio (mass fraction): 15% coal gangue, 65% fly ash, 4% stearic acid, 3% borax, 3% sorbitol, 13% attapulgite; the fly ash is ball milled to pass 200 mesh Sieve for standby, further ball mill the coal gangue and pass it through a 200-mesh sieve for standby; mix and stir the dry powder according to the proportioning quality, mill in a ball mill for 30 minutes, then add 20% (mass fraction) of water and mix evenly, granulate and shape, and the particle size is controlled to a diameter of 3mm , the molding pressure is 12.1MPa, and the pressure is maintained for 15S; the wet granules of the sample after compression molding are first dried in an oven at (100±1)°C for 2h, and then put into a muffle furnace, and the temperature is slowly raised below 300°C , and then gradually increase the temperature and fire to 500°C, hold for 30 minutes, heat up to 600°C, hold for 10 minutes, heat up to 700°C, hold for 10 minutes, heat up to 800°C, hold for 10...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
adsorption capacityaaaaaaaaaa
pore sizeaaaaaaaaaa
densityaaaaaaaaaa
Login to View More

Abstract

The present invention relates to a kind of fly ash CO 2 Preparation method of scavenger, and fly ash CO 2 The application of scavengers in the treatment of flue gas and in the storage and absorption of saline-alkali land and the improvement of saline-alkali land. 2 The method for preparing a scavenger includes step (1), the preparation of composite micro-ceramic particles, the raw material fly ash, inorganic waste, pore-forming agent, carbon-forming agent and additive machine are subjected to dry powder stirring and mixing, ball milling and water mixing and granulation and Drying and molding, step (2), surface modification, adding linear alkane benzene sulfonate sodium and the composite micro-ceramic particles obtained in step (1) into the ethanol coupling agent solution, and reaction drying under predetermined stability; step (3) , modification, adding the surface-modified composite micro-ceramic particles to the organic modifier methanol solution, stirring and drying. The invention adopts fly ash and inorganic waste to prepare CO 2 scavenger, not only can effectively use waste, but also obtain excellent fly ash CO through specific process subsidies 2 The performance of the trapping agent can realize the storage and improvement of the saline-alkali land.

Description

technical field [0001] The present invention relates to a kind of fly ash CO 2 Catching agent preparation method, and fly ash CO 2 The application of the capture agent in the treatment of flue gas and in the sequestration and absorption of saline-alkali land and the improvement of saline-alkali land belongs to the field of carbon neutral treatment agents and applications. Background technique [0002] On September 22, 2020, during the 75th session of the United Nations General Assembly, China proposed the CO 2 Emissions strive to peak before 2030, and strive to achieve carbon neutrality before 2060. Carbon neutrality means that enterprises, groups or individuals measure the total amount of greenhouse gas emissions directly or indirectly produced within a certain period of time, and offset the CO produced by themselves through afforestation, energy conservation and emission reduction, etc. 2 emissions, achieving CO 2 "zero emission". To achieve carbon neutrality, there a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B38/06C04B38/02C04B33/135C04B33/132C04B33/13C04B33/04C01B32/50
CPCC04B33/04C04B33/13C04B33/1321C04B33/1352C04B38/009C04B38/02C04B38/0645C04B38/0675C04B2235/6567C04B2235/661C04B2235/77C01B32/50C04B38/0074C04B38/0067C04B38/0054C04B33/132Y02P40/60
Inventor 苏斌苏文锦苏文雯
Owner BEIJING FAIRVIEW NEW TECH CO LTD
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com