Nano modified anti-rust special primer

An anti-rust primer and nano-modification technology, which is applied in the fields of metal anti-rust primer, protective and decorative coating, corrosion and anti-rust coating, and can solve the problems of high content of toxic substances, poor anti-rust performance, and poor quality. Stability and other issues, to achieve the effects of high density, improved salt spray resistance, and excellent low-temperature film-forming performance

Inactive Publication Date: 2006-10-11
彭志伟
View PDF1 Cites 24 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The technical problem to be solved by the present invention is to propose a nano-modified special anti-corrosion paint for many defects such as high content of toxic substances, non-environmental protection, high energy consumption, unstable quality, and poor anti-rust performance in the existing anti-corrosion

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] A, prepare antirust paint main agent and additive, selected raw material and proportioning are:

[0029] No. Raw material name %

[0030] 1 hydroxyacrylic resin 10.0

[0031] 2 Synthetic fatty acid resin 8.5

[0032] 3 nanometer iron oxide red 2.5

[0033] 4 Iron oxide yellow 12.0

[0034] 5 Talc 12.0

[0035] 6 nanometer zinc oxide 1.5

[0036] 7nm Silica 2.0

[0037] 8 Titanium iron powder 3.0

[0038] 9 Zinc iron phosphate 2.0

[0039] 10 Zinc tripolyphosphate 6.5

[0040] 11 CH series hyperdispersant 2.0

[0041] 12 Complex zinc phosphate 1.0

[0042] 13 Ethylene glycol ether acetate 10.0

[0043] 14 Silicone leveling agent 5.0

[0044] 15 Silicone defoamer 5.0

[0045] 16 Isopropanol 1.5

[0046] 17 Barium petroleum sulfonate 0.6

[0047] 18 titanate TC-F 0.2

[0048] 19 Dibutyl phthalate 0.2

[0049] 20 hydroxy acrylic resin 14.5

[0050] Total: 100.0

[0051] Production process and preparation method: put the above-men...

Embodiment 2

[0083] A, prepare antirust paint main agent and additive, selected raw material and proportioning are:

[0084] No. Raw material name %

[0085] 1 hydroxyacrylic resin 10.0

[0086] 2 Synthetic fatty acid resin 15.0

[0087] 3 Nanometer Iron Oxide Yellow 1.0

[0088]4 iron oxide red 5.5

[0089] 5 Talc 8.0

[0090] 6 Nanometer Iron Oxide Yellow 1.5

[0091] 7nm Silica 1.0

[0092] 8 Rutile titanium dioxide 3.0

[0093] 9 Zinc Phosphate 2.0

[0094] 10 Aluminum tripolyphosphate 7.0

[0095] 11 HK-03 organic dispersant 3.0

[0096] 12 Complex zinc phosphate 1.0

[0097] 13 Propylene glycol ether 10.0

[0098] 14 Silicone leveling agent 5.0

[0099] 15 Silicone defoamer 5.0

[0100] 16 Isopropanol 1.5

[0101] 17 Octanoic acid dicyclohexylamine 0.5

[0102] 18 titanate coupling agent TC-2 0.25

[0103] 19 Dioctyl phthalate 0.25

[0104] 20 hydroxy acrylic resin 19.5

[0105] Total: 100.0

[0106] Production technology and preparatio...

Embodiment 3

[0128] A, prepare antirust paint main agent and additive, selected raw material and proportioning are:

[0129] No. Raw material name %

[0130] 1 hydroxyacrylic resin 8.0

[0131] 2 Synthetic fatty acid resin 11.0

[0132] 3 Nano Iron Oxide Black 1.5

[0133] 4 iron oxide black 10.5

[0134] 5 Talc 8.0

[0135] 6 nanometer titanium dioxide 2.5

[0136] 7 Mica powder 1.0

[0137] 8 Carbon Black 3.0

[0138] 9 Titanium iron powder 5.5

[0139] 10 Phosphate aluminum 6.5

[0140] 11 SN5040 Dispersant 3.0

[0141] 12 Zinc phosphate 1.0

[0142] 13 Ethylene glycol ether acetate 10.0

[0143] 14 Silicone leveling agent 4.0

[0144] 15 Silicone defoamer 4.0

[0145] 16 polyhydroxyphenol 0.5

[0146] 17 titanate coupling agent G-2 0.25

[0147] 18 Dibutyl phthalate 0.25

[0148] 19 Hydroxy acrylic resin 19.5

[0149] Total: 100.0

[0150] Production process and preparation method: Put the above-mentioned raw materials with serial number...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Flash pointaaaaaaaaaa
Login to view more

Abstract

A nanometre-sized modified special rust-inhibiting primer is characterized in that it includes the following components (mass %): 29.0-60.0 % anti-corrosive paint host, 1.0-10.0 % nano oxide addition,5.0-15.0 % curing agent and 30.0-65 % diluent. The said anti-corrosive paint consists of rust-preventive material, coloring pigment, compounded resin and auxiliary agent, the curing agent is compounded by 75 % aromatic isocyanate, dimethylbenzene, butyl acetate, propanol and 2-butanol and the diluent is combination of alcohol and ester solvent. The invention has conducted adequate optimization and association for the components of the rust-inhibiting primer and its proportioning, which has largely reduced the contents of the toxic substance and the harmful substance in the total weight of the products, not only can guarantee the champion cryogenic film-forming property, but also can reduce the degree of pollution to the environment, which can effectively support the health of the maker, the user and the surrounding people, fitting requirement of the environmental protection, simultaneously can further improved the quality of the rust-inhibiting primer.

Description

technical field [0001] The invention relates to the technical field of metal coatings, in particular to a special metal anti-rust primer, which is mainly used for corrosion and anti-rust coating on the surface of mechanical equipment and metal structural parts, especially suitable for mechanical equipment, injection molding machines, die-casting machines, Protective and decorative coating for spark machines, CNC machining centers, air compressors, elevators, motors and other equipment and manufacturing industries. Background technique [0002] At present, most of the existing anti-corrosion and anti-rust paints are solvent-based paints, and their solvents are generally based on benzene organic solvents such as xylene, which are used as diluents for pigments, paints, etc., and their content is relatively high. Xylene is a colorless and transparent liquid, insoluble in water, soluble in ethanol and ether, toxic, volatile, can pollute air and environment, and seriously endanger...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D5/12C09D133/14
Inventor 彭志伟
Owner 彭志伟
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap