Gemini-like rosin segmented polyether sulfonate, preparation method and application thereof
A polyether sulfonate and gemini technology is applied in the field of gemini-like rosin block polyether sulfonate and its preparation and application. and other problems, to achieve the effect of easy control of molecular structure and molecular weight, good steric hindrance and good emulsion stability
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0026] Add 50 kilograms of masson pine rosin (produced by Guangxi Wuzhou Richeng Forestry Chemical Co., Ltd.) in a 100-liter stainless steel reaction kettle with agitator, constant pressure drop tank, thermometer, and pressure gauge, heat up to 100 ° C and melt, add 7.5 Kilograms of maleic anhydride (15% of rosin) were incubated at 180-190°C for 4 hours to prepare maleic rosin M1, whose analysis softening point reached 116°C;
[0027] Weigh 3.3 kg (9.34 mol) of maleic rosin M1, stir and heat up to 120°C for melting, add 0.21 kg of analytically pure potassium hydroxide, vacuumize and dehydrate for 0.3 hours, and pass through slowly at 120-140°C, 0-0.4MPa Inject 37.9kg (654.3mol) of propylene oxide (PO). After passing through PO, age and absorb to negative pressure, 28.8kg (653.9mol) of After aging and absorbing to negative pressure, the intermediate T1 was obtained, the measured hydroxyl value was 18.1mgKOH / g, and the relative molecular weight was about 7750g / mol;
[0028] Mix...
Embodiment 2
[0030] In the synthesis process of intermediate maleated rosin in embodiment 1, the mass of maleic anhydride charged is 30% of the mass of rosin, and the others remain unchanged. The intermediate maleated rosin M2 is obtained, with a softening point of 142° C., and the liquid chromatographic analysis of maleated rosin Content 68%;
[0031] The temperature of passing through propylene oxide is 155-160°C, and other things remain unchanged, to obtain the polymer surfactant SP-2702 ethylene glycol solution of the present invention;
Embodiment 3
[0033] In embodiment 1, 50 kilograms of filtrates are warmed up to 90~100 ℃, 1.6 kilograms of sodium hydroxide aqueous solution (mass concentration 50%) are added dropwise, micro-vacuum deammonia gas is neutral until the pH value of gas outlet stops, and product is the class of the present invention. Gemini rosin block polyether sulfonate sodium salt polymer surfactant SP-2703 ethylene glycol solution.
PUM
Property | Measurement | Unit |
---|---|---|
hydroxyl value | aaaaa | aaaaa |
softening point | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com