New technology for plating golden yellow on automotive hub
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A car wheel, golden yellow technology, applied in the field of electroplating process of car wheels, can solve the problems of high production cost, complicated process, environmental pollution, etc.
Inactive Publication Date: 2011-10-26
梁新中
View PDF0 Cites 1 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
However, the production cost of this process is high and the process is complicated. Sodium cyanide is used in the pre-copper plating process step, and chromic anhydride is used in the chrome plating process step. These chemical elements are extremely toxic and easily pollute the environment and cause harm to the human body.
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0006] The present invention will be further described below in combination with specific embodiments.
[0007] A number of plastic plating tanks with a length of 2m, a width of 0.8m and a depth of 1.5m form an electroplating production line. In the degreasing tank, the degreasing liquid is prepared by adding trisodium phosphate, sodium carbonate, disodium hydrogen phosphate, sodium pyrophosphate and metal cleaning agent with water, the pH value is 9-10, and it is heated to 60-80°C. After the automobile aluminum alloy wheel blank is polished, it is immersed in a degreasing liquid to clean and degrease. After soaking for 5-10 minutes, put it in a water tank for water washing, then put it into the pickling solution prepared by nitric acid, hydrofluoric acid and water in the pickling tank, soak for 0.5-1 minute, and pickle. After washing with water, put it into the zinc dipping bath prepared by sodium hydroxide, zinc oxide, ferric chloride, potassium sodium tartrate, sodium nitr...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
PUM
Login to View More
Abstract
The present invention discloses a technology for plating golden yellow on an automotive hub. The technology comprises the technical steps: galvanizing, pre-plating copper, brightly plating copper, plating nickel, plating golden yellow, and the like. The chemical composition formula contained in each L of plating solution is that: galvanizing solution comprises 220 to 240g of potassium chloride, 40 to 55g of zinc chloride, 30 to 35g of boric acid, and 15 to 25ml of brightener; copper pre-plating solution comprises 70 to 85g of copper pyrophosphate, 280 to 350g of pyrophosphoric copper potassium, 4 to 6ml of ammonia water, and 3 to 5ml of brightener; the bright copper plating solution comprises 200 to 220g of copper sulfate, 70 to 90g of sulfuric acid, 0.06 to 0.08g of chloride ion, and 4 to 8ml of brightener; nickel plating solution comprises 260 to 300g of nickel sulfate, 30 to 50g of nickel chloride, 30 to 40g of boric acid, 0.6 to 1ml of brightener, 8 to 12ml of softening agent, and 2 to 4ml of wetting agent; and golden yellow plating solution comprises 120 to 140g of imitation gold salt and 2 to 4ml of ammonia water. After the plating, water washing and drying are performed, and a polyurethane paint is sprayed on the surface of the automotive hub. The new technology for plating golden yellow on the automotive hub radically eliminates the damage and environmental pollution of sodium cyanide and chromic anhydride to human bodies; the plated golden yellow automotive hub is luxurious and attractive, has strong corrosion resistance, and is suitable for high-class automotive assembly.
Description
technical field [0001] The invention relates to an electroplating process, in particular to an electroplating process for an automobile wheel hub. Background technique [0002] With the continuous development of automobiles and the expansion of market demand, the variety of automobiles is increasing day by day, and the types are constantly improving, and the surface protection of automobile wheels is also being strengthened. Taking car wheels as an example, most of them are made of aluminum alloy, and the surface is electroplated with nickel-chromium coating. The process route is rough polishing, degreasing, water washing, pickling, zinc dipping, zinc stripping, secondary zinc dipping, pre-copper plating, acid plating Copper, nickel plating, chrome plating, water washing, and finally hot air drying, and water washing between each process step from pickling to chrome plating. The nickel plating process steps include semi-bright nickel plating, high sulfur nickel plating, brig...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.