Oil-resistant and wear-resistant modified PVC resin nanometer environment-friendly construction material and preparation method

A technology of PVC resin and building base material, applied in the field of building decoration materials, can solve the problems of insufficient stability of base material performance and low heat preservation performance of base material, and achieve excellent heat insulation performance, high flame retardant grade, excellent fire resistance and aging resistance performance effect

Inactive Publication Date: 2016-11-16
常熟市瑞思知识产权服务有限公司
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The performance of the base material in the prior art is not stable enough, especially the thermal insulation performance of the base material is not high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Oil-resistant and wear-resistant modified PVC resin nanometer environment-friendly construction material and preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] Embodiment 1 A kind of oil-resistant and wear-resistant modified PVC resin nano-environmental protection building substrate and its preparation method

[0018] An oil-resistant and wear-resistant modified PVC resin nano-environmental protection building base material, which includes the following raw materials: 50 parts of nitrile rubber, 30 parts of polyurethane rubber, 10 parts of 12-hydroxy methyl stearate, and 8 parts of magnesium methacrylate , 6 parts of vinyl tributylketoxime silane, 20 parts of nylon 66 staple fiber, 5 parts of polytrimethylene adipate, 10 parts of diethylene glycol dibenzoate, 8 parts of nitrile rubber modified phenolic resin, urethane 15 parts of rotropine, 5 parts of vacuum residue, 6 parts of pitch-based carbon fiber powder, 5 parts of non-halogenated organic phosphinate, 8 parts of hexamethylenetetramine, 2 parts of trimethylpentyltriethoxysilane Parts, 0.3 parts by weight of conductive mica powder, 0.2 parts by weight of nano-conductive gr...

Embodiment 2

[0024] Embodiment 2 A kind of oil-resistant and wear-resistant modified PVC resin nano-environmental protection building substrate and its preparation method

[0025] An oil-resistant and wear-resistant modified PVC resin nano-environmental protection building base material, which includes the following raw materials: 60 parts of nitrile rubber, 40 parts of polyurethane rubber, 15 parts of 12-hydroxymethyl stearate, and 12 parts of magnesium methacrylate , 10 parts of vinyl tributylketoxime silane, 25 parts of nylon 66 staple fiber, 10 parts of polytrimethylene adipate, 16 parts of diethylene glycol dibenzoate, 10 parts of nitrile rubber modified phenolic resin, urethane 20 parts of rotropine, 10 parts of vacuum residue, 8 parts of pitch-based carbon fiber powder, 7 parts of non-halogenated organic phosphinate, 10 parts of hexamethylenetetramine, 4 parts of trimethylpentyltriethoxysilane Parts, 0.5 parts by weight of conductive mica powder, 0.4 parts by weight of nano-conducti...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an oil-resistant and wear-resistant modified PVC resin nanometer environment-friendly construction materials and a preparation method. The construction material comprises organic silicon resin, organic solvent, vitrified micro-beads, titanium dioxide, quartz sand, silicon carbide micropowder, nanometer cerium oxide, ethanedioic polyester, light calcium carbonate, water-retaining resin polyvinyl alcohol, dispersant, thickener, brightener, zinc sulfide, foamed aluminum, hydroxy propyl methyl cellulose, nanosilicone dioxide, adhesive, cobalt naphthenate, molybdenum, nickel, propylene glycol, and chromium. The construction material is used for exterior walls of buildings specially, all performances of the exterior walls are effectively improved, nitrile rubber modifled bakelite, is mixed with the raw material and cured after being heated, melted resin turns into unmelted body structure rapidly from the linear structure. Mechanical performance is improved, and performance of high temperature resistance and low expansion is achieved. With pitch-based carbon fibers, mechanical performance of the material is enhanced, harmful gas and dust in the tail gas can be greatly absorbed and removed.

Description

technical field [0001] The invention relates to the technical field of building decoration materials, in particular to an oil-resistant and wear-resistant modified PVC resin nano-environmental protection building base material and a preparation method. Background technique [0002] The base material generally consists of four basic components: film-forming substances (resins), pigments (including extender pigments), solvents and additives. [0003] 1 Film-forming substances are the main components of coating films, including oils, oils and oils processed products, cellulose derivatives, natural resins and synthetic resins. Film-forming substances also include some non-volatile reactive diluents, which are the main substances that make the substrate firmly adhere to the surface of the object to be coated to form a continuous film. It is the basis of the substrate and determines the basic characteristics of the substrate. [0004] 2 Auxiliaries such as defoamers, leveling age...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L9/02C08L75/04C08L77/06C08L67/02C08K13/04C08K7/06C08K5/101C08K5/098C08K5/5465C08K5/103C08K3/04C08K3/34
CPCC08L9/02C08K2201/001C08K2201/011C08K2201/014C08L2201/02C08L2201/08C08L2205/035C08L2205/16C08L75/04C08L77/06C08L67/02C08K13/04C08K7/06C08K5/101C08K5/098C08K5/5465C08K5/103C08K3/04C08K3/34
Inventor 杨枫
Owner 常熟市瑞思知识产权服务有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap