Computer case toughness agent

A technology of computer shell and toughness agent, applied in the field of computer shell, can solve the problems of high cost, brittle material, heavy quality, etc., and achieve the effect of increasing the impact force and resistance of the shell and lasting use.

Inactive Publication Date: 2017-12-05
ANHUI SHENGLI PRECISION MFG TECH CO LTD
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Magnesium-aluminum alloys and titanium alloys are not very strong and wear-resistant, and the cost is relatively high.
The disadvantage of carbon fiber is that the cost is higher, and the molding is not as easy as the ABS shell, so the shape of the carbon fiber shell is generally relatively simple and lacks change, and the coloring is also difficult
The heat dissipation performance of polycarbonate PC is also better than that of ABS plastic, and the heat distribution is relatively uniform. Its biggest disadvantage is that it is relatively brittle and will break when it falls. Our common CDs are made of this material.
ABS engineering plastic is PC+ABS (engineering plastic alloy), the Chinese name in the chemical industry is plastic alloy, the biggest disadvantage of ABS engineering plastic is its heavy weight and poor thermal conductivity
[0004] In the comprehensive market, there are materials for the existing notebook computer casings. The casing materials are durable, wear-resistant and have good heat dissipation, but they are expensive. They are more suitable for high-end computers, but not suitable for the general public.
Polycarbonate and ABS engineering plastic materials are cheaper than magnesium-aluminum alloy and titanium alloy, but the materials are brittle and have poor thermal conductivity. As a notebook computer case, it will cause a series of problems due to quality problems.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A computer case toughness agent is made of the following raw material components in parts by weight:

[0024] 10 parts of hydrogenated terpene maleate, 12 parts of benzyltriethylammonium chloride, 13 parts of dimethyl maleate, 8 parts of alkyl polyglucoside, 9 parts of methyl pentyl acetate, epoxy furfuric acid 8 parts of butyl ester, 7 parts of carboxymethyl chitosan, 5 parts of polyvinylpyridine, 11 parts of polyvinyl acetate, 10 parts of silicon dioxide powder, 12 parts of hydroxyapatite-ferric oxide-zeolite composite material, 9 parts of plant extract oil, 20 parts of carbon fiber, 8 parts of butyl acrylate, 7 parts of modified high-temperature high-toughness epoxy resin, 16 parts of high-pressure low-density PE, 7 parts of graphene, 8 parts of polyamide fiber, and 13 parts of polyvinyl alcohol .

[0025] The preparation method of hydrogenated terpene maleic acid is as follows: select Winsor II single-phase microemulsion system to construct a reactor, use hydrogen ...

Embodiment 2

[0035] A computer case toughness agent is made of the following raw material components in parts by weight:

[0036] 7 parts of hydrogenated terpene maleate, 17 parts of benzyltriethylammonium chloride, 11 parts of dimethyl maleate, 8 parts of alkyl polyglucoside, 5 parts of methyl pentyl acetate, epoxy furfuric acid 4 parts of butyl ester, 6 parts of carboxymethyl chitosan, 5 parts of polyvinylpyridine, 13 parts of polyvinyl acetate, 12 parts of silicon dioxide powder, 12 parts of hydroxyapatite-ferric oxide-zeolite composite material, 8 parts of plant extract oil, 15 parts of carbon fiber, 6 parts of butyl acrylate, 7 parts of modified high-temperature high-toughness epoxy resin, 14 parts of high-pressure low-density PE, 12 parts of graphene, 7 parts of polyamide fiber, and 13 parts of polyvinyl alcohol .

[0037] The preparation method of hydrogenated terpene maleic acid is as follows: select Winsor II single-phase microemulsion system to construct a reactor, use hydrogen ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a computer case toughness agent, and relates to the technical field of a computer case, and the computer case is prepared from the following raw material components: hydrogenated terpene maleate, benzyl triethyl ammonium chloride, dimethyl maleate, alkyl polyglucoside, methyl pentyl acetate, epoxyfuroic oleic butyl ester, carboxymethyl chitosan, polyvinyl pyridine, polyvinyl acetate, silica powder, a hydroxyapatite-ferroferric oxide composite material, plant extract oil, carbon fiber, butyl acrylate, modified high temperature high toughness epoxy resin, high pressure low density PE, graphene, polyamide fiber and polyvinyl alcohol; the prepared computer case toughness agent has high pressure resistance, high temperature resistance, low temperature resistance, corrosion resistance, is not easy to break, and is durable to use, the computer material is hard and tough after use of the computer case toughness agent, case cracks and seams caused for the reason that the case is brittle and hard can be reduced, and impact force and impact resistance of the computer case can be increased, so that the computer case is touch or drop resistant.

Description

Technical field: [0001] The invention relates to the technical field of computer casings, in particular to a toughening agent for computer casings. Background technique: [0002] The shell of a notebook computer is not only the most direct way to protect the body, but also an important factor affecting its cooling effect, "weight" and aesthetics. Common casing materials for notebook computers include: alloy casings include aluminum-magnesium alloys and titanium alloys, plastic casings include carbon fiber, polycarbonate PC and ABS engineering plastics, and common casing materials for notebook computers include: alloy casings include aluminum-magnesium alloys and titanium alloys. Alloy, plastic shell has carbon fiber, polycarbonate PC and ABS engineering plastics. [0003] Magnesium-aluminum alloys and titanium alloys are not very strong and wear-resistant, and their cost is relatively high. The disadvantage of carbon fiber is that the cost is higher, and the molding is not...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L23/06C08L31/04C08L5/08C08L91/00C08L63/00C08L77/00C08L29/04C08K13/04C08K7/06C08K3/36C08K5/11C08K3/04
CPCC08L23/06C08L2201/08C08L2203/20C08L2205/035C08L2205/16C08L2207/066C08L31/04C08L5/08C08L91/00C08L63/00C08L77/00C08L29/04C08K13/04C08K7/06C08K3/36C08K5/11C08K3/04
Inventor 刘晓春乔印松黄现东全梦平钟远来
Owner ANHUI SHENGLI PRECISION MFG TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products