waterborne coating composition

A technology of water-based coatings and compositions, which is applied in the direction of anti-corrosion coatings, polyurea/polyurethane coatings, coatings, etc., and can solve the problems of water-based coating compositions such as gloss stability and insufficient weather resistance of smooth coating films

Active Publication Date: 2020-10-23
KANSAI PAINT CO LTD
View PDF10 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the water-based coating composition described in Patent Document 2 is insufficient in any one of smoothness, gloss stability of the coating film, and weather resistance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • waterborne coating composition
  • waterborne coating composition
  • waterborne coating composition

Examples

Experimental program
Comparison scheme
Effect test

manufacture example 1

[0112] Production example 1: Production example of acrylic resin solution

[0113] 368.6 parts of ethylene glycol monobutyl ether was charged into a 2-liter four-necked flask equipped with a stirrer, a thermometer, a reflux tube, and a nitrogen introduction tube, and after replacing with nitrogen, the mixture was kept at 85° C. while stirring.

[0114] In 3 hours, 130 parts of styrene, 144 parts of methyl methacrylate, 150 parts of n-butyl methacrylate, 250 parts of isobutyl methacrylate, 200 parts of n-butyl acrylate, 2 - A mixture of 426 parts of hydroxyethyl ester, 50 parts of acrylic acid, and 19.5 parts of 2,2'-azobis(2,4-dimethylvaleronitrile), and after the dropwise addition was completed, it was further kept at 85° C. for 1 hour, Then, a mixture of 65 parts of ethylene glycol monobutyl ether and 6.5 parts of 2,2'-azobis(2,4-dimethylvaleronitrile) was added dropwise over 1 hour. After completion of the dropwise addition, the temperature was maintained at 85°C for 1 hou...

manufacture example 2

[0115] Production example 2: Production example of polyester resin solution

[0116] In a reaction vessel equipped with a stirrer, a thermometer, a reflux pipe, a nitrogen introduction pipe, a rectification tower, and a water separator, 17 parts of trimethylolpropane, 1,6-hexanediol, and 21 parts, 15 parts of adipic acid, 29 parts of phthalic anhydride and 12 parts of Cardura E10P (manufactured by HEXION Specialty Chemicals, trade name, synthetic hyperbranched saturated fatty acid glycidyl ester) carry out condensation reaction, make resin acid value reach After 1.0 mgKOH / g or less, the toluene was solvent-removed under reduced pressure, and the reaction temperature was kept at 170°C.

[0117]Add 6 parts of trimellitic anhydride to the reaction product, make it react at 170°C, add dipropylene glycol monomethyl ether for 30 minutes, add dipropylene glycol monomethyl ether and cool to 85°C, neutralize with dimethylethanolamine, then form water with water A dispersion liquid was...

manufacture example 3

[0118] Production Example 3: Production Example of Polyisocyanate Compound No.1 Solution

[0119] A four-neck flask equipped with a stirrer, a thermometer, a reflux condenser, a nitrogen blowing pipe, and a dropping funnel was set as a nitrogen atmosphere, and 600 parts of hexamethylene diisocyanate and 2.5 parts of isobutanol were added, and the The temperature inside the reactor was maintained at 80°C for 2 hours. Then, 0.5 parts of a solution obtained by diluting the isocyanuration catalyst trimethyl-2-methyl-2-hydroxyethylammonium hydroxide to a concentration of 5% by mass with isobutanol was added to perform isocyanuration. After cyanurate reaction, 0.06 parts of phosphoric acid 85% aqueous solution was added to terminate the reaction.

[0120] Then, the reaction liquid was further kept at 160° C. for 1 hour to generate polyisocyanate. After cooling the reaction liquid to room temperature and filtering, unreacted hexamethylene diisocyanate was removed using a thin film ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
viscosityaaaaaaaaaa
hydroxyl valueaaaaaaaaaa
Login to View More

Abstract

The present invention provides a coating composition comprising a hydroxyl group-containing resin (a), barium sulfate (b) with an average particle diameter of 0.01 μm to 2.0 μm, a coloring pigment (c), and a viscosity of 150 mPa·s at 25° C. The polyisocyanate compound (d) and the silane coupling agent (e) above and below 800 mPa·s, wherein, based on the total solid content of 100 parts by mass of the hydroxyl-containing resin (a), the aqueous coating composition comprises 1 to 50 parts by mass of the barium sulfate (b), 1 to 100 parts by mass of the colored pigment (c), 10 to 150 parts by mass of the polyisocyanate compound (d) and 0.1 The silane coupling agent (e) in parts by mass to 10 parts by mass.

Description

technical field [0001] [Cross Reference to Related Application] [0002] This application claims priority based on Japanese Patent Application No. 2015-220860 specification filed on November 11, 2015 (the entire disclosure content of which is incorporated herein by reference). [0003] The invention relates to a water-based paint composition. Background technique [0004] Recently, various coating compositions are used for coating construction machines such as bulldozers, hydraulic excavators, and wheel loaders, or industrial machines. However, for coating compositions used for coating construction machinery or industrial machinery, there are problems such as the following when drying the coating film: (1) The heat capacity is large, and the heat of the drying oven cannot be sufficiently transmitted, and the curability is low. Insufficient; (2) There are many vertical parts, and the gloss of the matte coating film is unstable; (3) Furthermore, since construction machinery ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D175/04B05D7/14B05D7/24C09D5/08C09D7/61C09D7/63
CPCB05D7/14B05D7/24C09D5/08C09D175/04C09D7/40
Inventor 藤田充博胜田英明
Owner KANSAI PAINT CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com