Catalyst for preparing methyl isobutyl ketone from acetone by one-step method as well as preparation method and application thereof

A technology of methyl isobutyl ketone and catalyst, which is applied in chemical instruments and methods, physical/chemical process catalysts, metal/metal oxide/metal hydroxide catalysts, etc., can solve the problems of high cost and poor catalyst activity. , to achieve the effect of strong adaptability, low cost and easy control

Active Publication Date: 2019-05-03
CHINA PETROLEUM & CHEM CORP +1
View PDF8 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] In order to solve the technical problems of poor activity and high cost of the catalysts existing in the prior art, the present invention proposes a new catalyst for the preparation of methyl isobutyl ketone by using acetone of a new non-noble metal

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Catalyst for preparing methyl isobutyl ketone from acetone by one-step method as well as preparation method and application thereof
  • Catalyst for preparing methyl isobutyl ketone from acetone by one-step method as well as preparation method and application thereof
  • Catalyst for preparing methyl isobutyl ketone from acetone by one-step method as well as preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0041] Dissolve 30g of nano-titanium dioxide in 20mL of ethanol to make mixture I, weigh 115g of alumina powder, add 5g of turnip powder and 10g of citric acid and mix well to make mixture II, add mixtures I and II to the kneader Mix evenly, and add 6.0mL of dilute nitric acid and 65mL of water to stir and knead to form, and the obtained carrier is dried and roasted at 1050°C to obtain a titanium-modified carrier; 19.5g of copper nitrate and 0.16g of palladium chloride are weighed and dissolved in Impregnate 95g of the carrier prepared above with equal volume of 30mL water, dry at 120°C for 2h after impregnation, decompose at 350°C for 3h, then reduce the catalyst with a mixture of 5vol% hydrogen and 95vol% nitrogen according to the temperature program, and raise the temperature to 280°C After constant temperature reduction for 4 hours, the catalyst was obtained after cooling down. According to X-fluorescence test and analysis, the catalyst contained 3.85 parts of copper, 0.62 ...

Embodiment 2

[0043] Dissolve 20.4g of nano-titanium dioxide in 15mL of isopropanol to make mixture I, weigh 25g of silicon dioxide and 100g of alumina powder and add 6g of turnip powder and 12g of citric acid and mix well to make mixture II. Mixing materials I and II were added to a kneader and mixed evenly, and 3.5mL of dilute sulfuric acid and 70mL of water were added to stir and knead to shape, and the obtained carrier was dried and roasted at 970°C to obtain a titanium-modified carrier; weigh 20g of copper nitrate and Dissolve 0.15g of palladium chloride in 36mL of water and impregnate 95g of the above-prepared carrier in equal volume. After impregnation, dry at 100°C for 2h, decompose at 380°C for 3h, and then use a mixed gas of 5vol% hydrogen and 95vol% nitrogen according to the temperature program method. Reduce the catalyst, raise the temperature to 270°C and reduce it at a constant temperature for 4 hours. After cooling down, the catalyst is prepared. According to X-fluorescence te...

Embodiment 3

[0045] Dissolve 10.8g of butyl titanate in 12mL of ethanol to make a mixture I, weigh 75g of silicon dioxide and 55g of alumina powder, add 8g of turnip powder and 10g of citric acid and mix well to make a mixture II, Mix materials I and II into a kneader and mix them evenly, and then add 7.5mL of dilute nitric acid and 77mL of water to stir and knead to form the obtained carrier. After drying and roasting at 1150°C, a titanium-modified carrier is obtained; weigh 9.1g of copper nitrate Dissolve 0.1g of palladium chloride in 25mL of water and impregnate 95g of the above-prepared carrier in equal volume. After impregnation, dry at 110°C for 2h, decompose at 350°C for 3h, and then use a mixture of 5vol% hydrogen and 95vol% nitrogen according to the temperature program method. Gas reduction catalyst, heating up to 240°C and constant temperature reduction for 6 hours, the catalyst was prepared after cooling down, and analyzed by X-fluorescence test, the catalyst was 1.59 parts of co...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a catalyst for preparing methyl isobutyl ketone from acetone by a one-step method as well as a preparation method and application thereof. The total weight of the catalyst is100 parts by weight, and the catalyst comprises the following components in parts by weight: a, 0.5-8 parts of at least one of copper or copper oxides; b, 0.01-0.2 part of at least one of palladium orpalladium oxides; and c, 82-99.49 parts of a carrier, wherein the carrier is selected from at least one of silicon oxide, aluminum oxide and zirconium oxide modified by high-temperature roasted titanium. The catalyst can be used under milder reaction conditions, the yield of the methyl isobutyl ketone is higher than that of a palladium/resin catalyst which is commonly used by an existing industrial device, and meanwhile byproduct methyl isobutyl alcohol is produced; in addition, the catalyst shows ideal stability. In addition, the cost of the catalyst is remarkably lower than that of an existing palladium catalyst, and the catalyst has relatively good economic benefits and is worthy of popularization and application.

Description

technical field [0001] The invention relates to the field of catalysts, and more particularly, relates to a catalyst for preparing methyl isobutyl ketone by a one-step method from acetone, a preparation method and application thereof. Background technique [0002] Methyl isobutyl ketone (MIBK for short) is an important solvent and chemical intermediate. It has attracted much attention because of its excellent performance. It has an aromatic ketone smell, is colorless and transparent, has a medium boiling point, and has a very strong solvency. , miscible with many organic solvents such as alcohol, benzene, ether, etc., can be used as paint, ethyl cellulose, nitrocellulose, audio and video tapes, paraffin, various natural or synthetic resin solvents, dewaxing agents, rare earth metal extractants, The raw materials of polymerization initiators, surfactants, pharmaceuticals, pesticide extractants and rubber antioxidants are currently relatively in short supply fine petrochemical...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B01J23/89C07C45/73C07C49/04
Inventor 唐国旗田保亮李宝芹
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap