Preparation method, product of hot-melt self-adhesive, and application of hot-melt self-adhesive in making self-adhesive bandage

A self-adhesive and hot-melt technology, applied in the direction of adhesives, adhesive types, heat-activated films/sheets, etc., can solve problems such as high emulsion prices, skin allergies, and unfriendly environment, and save equipment investment and production space , Low skin irritation and simple preparation process

Active Publication Date: 2020-01-14
杭州高斯博医疗用品有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, there are two main systems of self-adhesive used for self-adhesive bandages on the market. One is the traditional natural latex as self-adhesive, which is characterized by convenient sources, good self-absorption of products, good air permeability, and skin contact. Comfortable, moderate cost, etc., but the disadvantage is that natural latex contains protein, which will cause skin allergies to some people, and due to the existence of protein, the products usually have peculiar smell, moldy and deteriorated during the storage period, and the quality of the products is unstable
The second is to use synthetic rubber as self-adhesive. Since the softening point of the directly obtained synthetic rubber is generally high, it is not suitable for direct coating. The use of synthetic rubber self-adhesive usually adopts solvent coating and emulsion coating. The method of coating is to directly dissolve the synthetic glue in the solvent for use, which has the characteristics of convenient use, rapid drying, high production efficiency, low processing cost, and good comprehensive performance of the product, but the disadvantage is that a large amount of organic solvents are needed in the production process , not friendly to the environment, poor operating environment, and there are potential safety hazards, relatively high costs and other disadvantages, especially environmental protection issues, has become a bottleneck that inhibits the survival of enterprises; emulsion coating is to convert solvent-based synthetic adhesives into water emulsions. It is characterized by safe operation process, environmental protection, low skin allergy to the bandage, and good comprehensive performance of the product, but the price of the emulsion is high, the processing cost of the product is high, and the production efficiency is not high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method, product of hot-melt self-adhesive, and application of hot-melt self-adhesive in making self-adhesive bandage
  • Preparation method, product of hot-melt self-adhesive, and application of hot-melt self-adhesive in making self-adhesive bandage
  • Preparation method, product of hot-melt self-adhesive, and application of hot-melt self-adhesive in making self-adhesive bandage

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0054] Firstly, the polyisoprene rubber synthesized from the raw material is sliced, the double-roll mill is preheated, the roll temperature is kept between 55-65°C, the roll speed is controlled at 16-18r / min, and the speed ratio of the front and rear rolls is adjusted to 1. : 1.15~1.18, then add the sliced ​​rubber into the open mill for masticating, thin pass 3 times, after the plasticized rubber is chopped by a shredder, it is sealed and stored for later use.

[0055] Then, add 109.50kg of raw materials methyl methacrylate, 790.00kg of isooctyl acrylate, 100.00kg of dioctyl adipate, and 0.50kg of benzoyl peroxide into the reaction kettle with a reflux condenser, start the stirrer, and heat The temperature of the reaction system is 85-90°C, and the reaction is maintained at this temperature. When the reaction becomes viscous, the heating is stopped (about 3 hours), and the reaction is completed. When the temperature is lowered to below 40°C, the material can be discharged to ...

Embodiment 2

[0060] Firstly, the polyisoprene rubber and styrene-butadiene rubber synthesized by the raw materials are sliced ​​separately, the double-roll mill is preheated, the roller temperature is kept between 50-60°C, and the roller speed is controlled at 16-18r / min. Before and after adjustment The speed ratio of the rollers is 1:1.18~1.20, and then the sliced ​​rubber is added to the open mill for mastication. The polyisoprene rubber is thinly passed 3 times, and the styrene-butadiene rubber is thinly passed 5 times. The plasticized rubber is cut After shredding with a shredder, keep it sealed for future use.

[0061] Then, 99.00 kg of methyl methacrylate, 560.00 kg of isooctyl acrylate, 140.00 kg of dodecyl methacrylate, 200.00 kg of dioctyl phthalate, and 1.00 kg of azobisisobutyronitrile were added to the reflux In the reaction kettle of the condenser, start the agitator, heat the temperature of the reaction system to 90-95°C, and maintain the reaction at this temperature, stop he...

Embodiment 3

[0066] Firstly, the raw materials synthesized polyisoprene rubber, SIS rubber and EPDM rubber were sliced ​​separately, and the double-roll mill was preheated, the roller temperature was kept between 60-70°C, and the roller speed was controlled at 16-18r / min, adjust the speed ratio of the front and rear rollers to 1:1.20~1.25, and then add the sliced ​​rubber into the open mixer for mastication. The polyisoprene rubber and SIS rubber are thinly passed 3 times, and the EPDM rubber is thinly passed. It can be passed 5 times. After the plasticized rubber is chopped by a shredder, it is sealed and stored for later use.

[0067] Then, the raw materials methyl methacrylate 103.00kg, butyl acrylate 559.75kg, dodecyl methacrylate 186.50kg, dioctyl phthalate 100.00kg, dioctyl sebacate 50.00kg, di-t-butyl Add 0.25 kg of base peroxide, 0.50 kg of azobisisobutyronitrile, etc. into the reaction kettle with reflux condenser, start the agitator, heat the temperature of the reaction system t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
peel strengthaaaaaaaaaa
peel strengthaaaaaaaaaa
peel strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a preparation method of a hot-melt self-adhesive. The method comprises the following steps: (1) making a plasticated rubber by using a thermoplastic polymer; (2) making a polyacrylate tackifier by using an acrylate monomer; and (3) mixing the plasticated rubber obtained in the step (1), the polyacrylate tackifier obtained in the step (2), and remaining components accordingto a ratio at 80-150 DEG C to obtain the hot-melt self-adhesive. The invention also discloses the hot-melt self-adhesive and an application in making a self-adhesive bandage. The self-adhesive and theself-adhesive bandage which are prepared by the method have many advantages such as convenient raw material sources, simple production process, safe use, environmental friendliness and low cost of the hot-melt self-adhesive, and good comprehensive performance and low skin irritation of bandage products.

Description

technical field [0001] The invention belongs to the technical field of synthetic adhesives, and in particular relates to a preparation method and product of hot-melt self-adhesive and its application in the production of self-adhesive bandages. Background technique [0002] Self-adhesive adhesive, referred to as self-adhesive, is mainly used for the production of self-adhesive bandages. Self-adhesive bandages, also known as self-adhesive elastic bandages or self-adhesive elastic bandages, belong to medical sporting goods and are suitable for sports, training, outdoor sports, field operations, industrial operation protection, military injuries, surgical and orthopedic wound dressings, and limb immobilization. Limb sprains, soft tissue injuries, joint swelling and pain bandaging, orthopedic surgery, etc. Self-adhesive bandages are usually made of cotton yarn, cotton spandex core-spun yarn, medical intermediate self-adhesive and other materials. Among them, the performance of...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09J7/35C09J109/00C09J109/06C09J133/08C09J153/02C09J123/16C09J11/04C09J11/06C09J11/08C09J7/21
CPCC08K2003/2296C08K2003/265C08K2201/014C08L2205/02C08L2205/025C08L2205/035C09J11/04C09J11/06C09J11/08C09J109/00C09J7/21C09J7/35C09J2301/122C08L33/08C08K13/02C08K3/36C08K5/13C08K5/47C08K3/22C08L9/06C08K3/26C08L53/02C08L23/16C08K5/18C08K5/11
Inventor 来焱杨震铎何亚荣王杰
Owner 杭州高斯博医疗用品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap