A kind of graphyne-based composite material catalyst and its preparation method and application

A technology of composite materials and graphyne, which is applied in the field of graphyne-based composite catalysts and its preparation and application, and can solve the problems of low gas metal dispersion and low mass transfer

Active Publication Date: 2020-08-21
ZHEJIANG UNIV OF TECH
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0009] The purpose of the present invention is to provide a graphyne-based composite catalyst and its preparation method and application. The present invention fundamentally solves the shortcomings of low gas metal dispersion and low mass transfer in the supported ionic liquid catalyst system

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of graphyne-based composite material catalyst and its preparation method and application
  • A kind of graphyne-based composite material catalyst and its preparation method and application
  • A kind of graphyne-based composite material catalyst and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0086] Catalyst preparation:

[0087] 1) Select 10 g of graphdiyne powder, select 0.1 g of melamine and dissolve it in 5 mL of toluene, spray the obtained impregnating solution onto the surface of the aforementioned carrier, and put it into a quartz boat in a tube furnace, in a nitrogen atmosphere at 800 ° C Calcined for 2h, the obtained solid sample was set aside.

[0088] 2) Dissolve 0.08g of triphenylmethylphosphine bistrifluoromethanesulfonimide salt and 0.02g of triphenylethylphosphine bromide in 10mL of toluene, stir well, then add the solid sample obtained in step 1) , impregnated for 2 hours, and dried at 180°C for later use. Wherein the mass loading of ionic liquid is 1%.

[0089] 3) Dissolve 4.23g of copper chloride in 2.12mL of toluene, stir evenly, add the sample obtained in step 2), dip in an external 0.2kV static electric field for 2h, and dry at 180°C for later use. Wherein the mass loading of copper element is 20%.

[0090] 4) 14.43 g of the solid sample ob...

Embodiment 2

[0094] Catalyst preparation:

[0095] 1) Select 10 g of graphdiyne film, select 2.0 g of boric acid and dissolve it in 100 mL of nitrogen-methylpyrrolidone, spray the obtained impregnating solution onto the surface of the aforementioned carrier, and put it into a quartz boat in a tube furnace. Calcined in an argon atmosphere for 10 h, the obtained solid sample was used for future use.

[0096] 2) Take 0.6g of 1-propyl-2,3-dimethylimidazole bistrifluoromethanesulfonimide salt and 1.4g of 1-hexyl-2,3-dimethylimidazole bistrifluoromethanesulfonimide The salt ionic liquid was dissolved in 10 mL of nitrogen methyl pyrrolidone, and after stirring evenly, the solid sample obtained in step 1) was added, soaked for 10 h, and dried at 180°C for use. Wherein the mass loading of ionic liquid is 20%.

[0097] 3) Dissolve 0.2g of rhodium chloride in 1.6mL of nitrogen methylpyrrolidone, stir evenly, add the sample obtained in step 2), dip in an external 4kV static electric field for 3h, an...

Embodiment 3

[0102] Catalyst preparation:

[0103] 1) Select 10 g of copper-based graphyne, select 1.5 g of triphenylphosphine and dissolve it in 50 mL of nitrogen-nitrogen dimethylformamide, spray the obtained impregnating solution onto the surface of the aforementioned carrier, and put it into the quartz crystal in the tube furnace. In the boat, it was calcined in a helium atmosphere at 500°C for 6 hours, and the obtained solid sample was used for future use.

[0104] 2) Dissolve 0.3g of 1-butyl-3-methylimidazolium hexafluorophosphate and 0.7g of nitrogen-methylpyrrolidone hydrochloride in 50mL of nitrogen-nitrogen dimethylformamide, stir well, and add to step 1) The obtained solid samples were soaked for 5 hours and dried at 180°C for use. Wherein the mass loading of ionic liquid is 10%.

[0105] 3) Dissolve 0.103g of ruthenium chloride in 0.5mL of nitrogen-nitrogen dimethylformamide, stir evenly and add the sample obtained in step 2), dipping in an external 2.0kV static electric field ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a graphdiyne-based composite material catalyst and a preparation method and application thereof. The dispersing effect of metal in the graphdiyne-based composite material catalyst is better, the catalytic activity is higher, the stability is better, and the metal is stabilized on the outer surface layer of the catalyst through the form of coordination with ionic liquid, so that the influence of mass transfer is reduced, and the dispersity of the metal is improved meanwhile. According to the graphdiyne-based composite material catalyst and the preparation method and application thereof, an external static electric field is introduced into the preparation of the ionic-liquid-loaded metal-based catalyst for the first time, the enrichment of metal active centers on the surface layer of the ionic liquid is promoted, since the metal active centers of the catalyst are distributed on the surface layer of the ionic liquid, the influence of substrate diffusion is reduced,and under the evaluated reaction condition, the induction period of the catalyst disappears.

Description

[0001] (1) Technical field [0002] The invention relates to a graphyne-based composite material catalyst, a preparation method and application thereof. [0003] (2) Background technology [0004] Vinyl chloride is the monomer of polyvinyl chloride (PVC), one of the five largest synthetic resins in the world, and is mainly produced by the calcium carbide acetylene method and the petroleum ethylene method. China's coal-rich, oil-poor, and gas-poor energy reserves determine that the calcium carbide acetylene method will continue to be the main process for the production of vinyl chloride in my country for a long time to come, that is, mercuric chloride catalyzes the reaction of acetylene and hydrogen chloride to produce vinyl chloride. However, the highly toxic mercuric chloride catalyst seriously pollutes the environment and endangers human health. Therefore, the development of non-mercury catalysts is very necessary for the sustainable development of the calcium carbide acetyl...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01J31/02B01J31/22B01J31/24B01J37/34C07C17/08C07C21/06
CPCB01J31/0292B01J31/1815B01J31/183B01J31/24B01J37/342B01J2231/32B01J2531/16B01J2531/18B01J2531/821B01J2531/822C07C17/08C07C21/06
Inventor 赵佳李小年丰枫姚楠王柏林陆金跃王赛赛邵淑娟方正
Owner ZHEJIANG UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com