A kind of polyester fdy hot-melt fiber and preparation method thereof

A hot-melt fiber and polyester technology, which is applied in the field of polyester fiber, can solve the problems of reducing the effective content of catalyst, increasing the content of antimony in polyester, and corrosion of polymerization equipment, etc., and achieves a technology suitable for popularization and use, low melting point, and improved quality. Effect

Active Publication Date: 2021-06-15
扬州富威尔复合材料有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Moreover, ethylene glycol, which is used as a raw material for polyester synthesis, contains dozens of ppm of hydrogen sulfide (residual in petrochemical or coal chemical industry). For a long time, hydrogen sulfide will cause corrosion to polymerization equipment and cause catalyst poisoning in the polymerization process. (Generation of antimony sulfide reduces the effective content of the catalyst); therefore, in order to make the polymerization proceed smoothly, the amount of catalyst used is usually increased, which affects the polyester from two aspects: one is that the antimony sulfide is yellow and will enter the In polyester, the color is affected (b value increases); the second is the increase of catalyst, which increases the content of antimony in polyester

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of polyester fdy hot-melt fiber and preparation method thereof
  • A kind of polyester fdy hot-melt fiber and preparation method thereof
  • A kind of polyester fdy hot-melt fiber and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] A kind of preparation method of polyester FDY hot-melt fiber, concrete process is as follows:

[0045] (1) Esterification reaction;

[0046] After preparing terephthalic acid, isophthalic acid, ethylene glycol, diethylene glycol, calcium sulfonate isophthalate, macromolecular modulus modifier and zinc oxide into a slurry, the temperature is 235 ° C and the pressure is React under the nitrogen atmosphere of 0.25MPa, reach 90% of theoretical value to water distillation amount; Wherein, the mol ratio of terephthalic acid, isophthalic acid, ethylene glycol, diethylene glycol and calcium sulfonate isophthalate is 1:0.4:1.9:0.1:0.02; when the macromolecular modulus regulator is polybutylene adipate with a number average molecular weight of 550, its mass addition is 3% of the phthalic acid mass addition; The mass addition is 0.01% of the mass addition of phthalic acid;

[0047] (2) polycondensation reaction;

[0048] Add antimony trioxide and triphenyl phosphate to the syst...

Embodiment 2

[0062] A kind of preparation method of polyester FDY hot-melt fiber, concrete process is as follows:

[0063] (1) Esterification reaction;

[0064] After preparing terephthalic acid, isophthalic acid, ethylene glycol, diethylene glycol, zinc isophthalic acid sulfonate, macromolecular modulus regulator and zinc oxide into a slurry, the temperature is 230 ° C and the pressure is Reaction under the nitrogen atmosphere of 0.26MPa, reach 91% of theoretical value to water distillation amount; Wherein, the mol ratio of terephthalic acid, isophthalic acid, ethylene glycol, diethylene glycol and isophthalic acid zinc sulfonate is 1:0.5:1.8:0.2:0.01; when the macromolecular modulus regulator is polytrimethylene adipate with a number average molecular weight of 500, its mass addition is 4% of the phthalic acid mass addition; the mass addition of zinc oxide The amount is 0.012% of the mass addition of phthalic acid;

[0065] (2) polycondensation reaction;

[0066] Add ethylene glycol a...

Embodiment 3

[0071] A kind of preparation method of polyester FDY hot-melt fiber, concrete process is as follows:

[0072] (1) Esterification reaction;

[0073] After preparing terephthalic acid, isophthalic acid, ethylene glycol, diethylene glycol, magnesium sulfonate isophthalate, macromolecular modulus regulator and zinc oxide into a slurry, the temperature is 238 ° C and the pressure is React under the nitrogen atmosphere of 0.28MPa, reach 90% of theoretical value to water distillation amount; Wherein, the mol ratio of terephthalic acid, isophthalic acid, ethylene glycol, diethylene glycol and magnesium sulfonate isophthalate is 1:0.4:1.9:0.2:0.02; when the macromolecular modulus regulator is polyethylene adipate with a number average molecular weight of 600, its mass addition is 3% of the phthalic acid mass addition; The mass addition is 0.011% of the mass addition of phthalic acid;

[0074] (2) polycondensation reaction;

[0075] Add antimony acetate and trimethyl phosphite to the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
glass transition temperatureaaaaaaaaaa
glass transition temperatureaaaaaaaaaa
Login to View More

Abstract

The present invention relates to a kind of polyester FDY hot melt fiber and preparation method thereof, with phthalic acid (terephthalic acid and isophthalic acid), ethylene glycol, diethylene glycol, glass transition temperature regulator ( Formic acid sulfonate), macromolecular modulus regulator (fatty acid ester or long-chain diol with carbon number greater than or equal to 5) and zinc oxide as reaction raw materials to prepare low-melting point polyester, and spin it according to FDY process Obtain polyester FDY hot-melt fiber. The obtained polyester FDY hot-melt fiber is made of low-melting point polyester, and the molecular chain of low-melting point polyester is composed of phthalic acid segment, ethylene glycol segment, diethylene glycol segment, and glass transition temperature regulator chain. Segment and macromolecular modulus regulator chain segment composition; A kind of preparation method of polyester FDY hot-melt fiber of the present invention reduces the impact of hydrogen sulfide in the polymerization process on polyester hot-melt fiber and reduces the initial modulus of fiber While avoiding fiber adhesion, the method is simple and the fiber application range is wide.

Description

technical field [0001] The invention belongs to the technical field of polyester fibers, and relates to a polyester FDY hot-melt fiber and a preparation method thereof. Background technique [0002] Polyester fiber is durable, wrinkle-resistant and crisp, has good washability and wearability, and is widely used. It is one of the synthetic fibers with the largest demand and the fastest development speed. Low melting point polyester is a new type of modified polyester that lowers the melting point (100-210°C) by adding a variety of modifying components during the polymerization of ordinary polyesters to change the molecular structure of PET. Low-melting point polyester is widely used in the production of non-woven fabrics for clothing or electrical insulation non-woven fabrics. The fibers made from it are mixed in ordinary polyester fiber nets, and only need to be heated to its melting point to produce bonding. After cooling and solidification Strong bonding can improve the t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D01F6/92D01F1/10C08G63/688C08G63/672C08K3/22
CPCC08G63/672C08G63/6886C08K3/22C08K2003/2296D01F1/10D01F6/92
Inventor 谭平乃符呈生
Owner 扬州富威尔复合材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com