A kind of anti-aging fiberglass material and preparation method thereof

A fiberglass and anti-aging technology, applied in the field of composite materials, can solve problems such as aging, performance defects, and affecting the performance and service life of FRP products, so as to improve aging resistance and mechanical strength, aging resistance and strength, Good dispersion effect

Active Publication Date: 2022-04-22
CHENGDE RENHE MINING CO LTD
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, FRP is a fiber-reinforced plastic, which has the common defects of plastics, and is prone to aging phenomena. It is easy to cause performance defects under the action of ultraviolet rays, mechanical stress, wind, sand, rain, snow, media, etc., especially in marine environments, long-term exposure to ultraviolet rays, seawater, etc. The corrosion caused by the influence of ocean, atmosphere and marine organisms has seriously affected the performance and service life of FRP products.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of anti-aging fiberglass material and preparation method thereof
  • A kind of anti-aging fiberglass material and preparation method thereof
  • A kind of anti-aging fiberglass material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0041] Preparation of illite functional powder material: 100 grams of illite powder is acid-washed with sulfuric acid and then washed with water to neutrality. The mass fraction of each component of illite powder is: SiO 2 72%, Al 2 o 3 18%, K 2 O 6%, other metal oxides 4%, the particle size of the illite powder is 325 mesh, the amount of acid is 10% of the mass of the illite powder, the pickling temperature is 90°C, the pickling time is 2h, and dried to contain water rate is less than 1%, add silane coupling agent KH550, the amount of silane coupling agent KH550 is 0.5% of the mass of illite powder, the stirring temperature of adding silane coupling agent KH550 is 50°C, and the stirring time is 2h. Obtain illite functional powder material.

[0042] Preparation of aging-resistant FRP material: Weigh 100 grams of isobenzene-type unsaturated polyester resin 199# resin, 2 grams of styrene, 2 grams of methyl ethyl ketone peroxide, 1 gram of cobalt naphthenate, 110 grams of glas...

Embodiment 2

[0045] Preparation of illite functional powder material: pickling illite powder with nitric acid and washing with water until neutral, the mass fraction of each component of illite powder is: SiO 2 75%, Al 2 o 3 14%, K 2 O 9%, other metal oxides 2%, the particle size of the illite powder is 500 mesh, the amount of acid is 20% of the mass of the illite powder, the pickling temperature is 90°C, the pickling time is 2.5h, and dried to The water content is less than 1%, add silane coupling agent KH560, the dosage of silane coupling agent KH560 is 1.0% of the mass of illite powder, the stirring temperature for adding silane coupling agent KH560 is 50°C, the stirring time is 2h, stir Finally, the illite functional powder material is obtained.

[0046] Preparation of aging-resistant FRP material: Weigh 100 grams of bisphenol A type unsaturated polyester resin (197C# resin), 4 grams of styrene, 2 grams of ethylenediamine, 2 grams of N,N-dimethylaniline, and 100 grams of glass fiber...

Embodiment 3

[0049] Preparation of illite functional powder material: pickling illite powder with sulfuric acid, nitric acid, hydrochloric acid and washing with water until neutral, the mass fraction of each component of illite powder is: SiO 2 78%, Al 2 o 3 16%, K 2 O 5.8%, other metal oxides 0.2%, the particle size of the illite powder is 800 mesh, the amount of acid is 30% of the mass of the illite powder, the pickling temperature is 90°C, the pickling time is 3h, and dry to water rate is less than 1%, add silane coupling agent KH792, the amount of silane coupling agent KH792 is 2.0% of the mass of illite powder, the stirring temperature for adding silane coupling agent KH792 is 50°C, the stirring time is 2h, after stirring The illite functional powder material is prepared.

[0050] Preparation of anti-aging FRP material: Weigh 100 grams of vinyl ester type unsaturated polyester resin W2-3# resin, 8 grams of styrene, 3 grams of benzoyl peroxide, 2 grams of N,N-dimethylaniline, glass ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention provides an aging-resistant FRP material, which is prepared from the following raw materials in parts by weight: 100 parts of unsaturated polyester resin, 2-8 parts of styrene, 1-3 parts of curing agent, 1-3 parts of accelerator, 80-120 parts of glass fiber, 10-40 parts of illite functional powder material, 1-3 parts of coupling agent, 1-2 parts of zinc oxide, 5-6 parts of graphene. The preparation method is to pickle the illite powder, wash it with water until it is neutral, dry it, and use a coupling agent for secondary modification to obtain the illite functional powder material. The addition of illite functional powder material and other raw materials of the present invention can increase the degree of cross-linking between polymer chains, and effectively improve the aging resistance and mechanical strength of the FRP material. The aging-resistant FRP material of the present invention is especially suitable for ships and other marine applications. environment, its salt spray resistance, aging resistance and strength are significantly improved compared with ordinary FRP materials.

Description

technical field [0001] The invention belongs to the technical field of composite materials, and relates to an aging-resistant glass fiber reinforced plastic material and a preparation method thereof. Background technique [0002] FRP, also known as fiber-reinforced plastic, refers to a composite material made of glass fiber reinforced unsaturated polyester, epoxy resin and phenolic resin matrix, glass fiber, carbon fiber or boron fiber as reinforcing materials, and made through a composite process. Due to the different types of resin used, it is called polyester FRP, epoxy FRP, and phenolic FRP. The material is light and hard, non-conductive, high mechanical strength, good insulation, less recycling, good thermal performance, and corrosion resistance. The relative density of FRP is between 1.2-2.0, only 1 / 4-1 / 5 of that of carbon steel, but its tensile strength is close to or even higher than that of carbon steel, and its specific strength can be compared with that of high-g...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L67/06C08K13/06C08K9/06C08K7/14C08K3/34C08K3/22C08K3/04C08K5/098
CPCC08K13/06C08K9/06C08K7/14C08K3/346C08K3/22C08K3/042C08K5/098C08L2201/08C08L2312/00C08K2003/2296C08L67/06
Inventor 郎宝龙隋英丹王春侠
Owner CHENGDE RENHE MINING CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products