Room temperature super-fast curing double-component solvent-free polyurethane structural adhesive and preparation method and use method thereof

A solvent-free polyurethane, ultra-fast technology, applied in polyurea/polyurethane adhesives, adhesives, adhesive types, etc. Solve problems such as long glue time, achieve high peel strength, excellent adhesive performance, and simple preparation process

Inactive Publication Date: 2018-02-02
WENZHOU INST OF BIOMATERIALS & ENG
View PDF2 Cites 37 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The patent application number 201610820437.9 reports a solvent-free and non-foaming polyurethane structural adhesive and its preparation method. Adhesive operating time adjustable range is narrow and the problem of foaming in the curing process, but its gel time is 30min ~ 80min, the gel time is too long, which is not conducive to the rapid fixation of the adhered material and the rapid mass production of the factory

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] A room temperature super fast curing two-component solvent-free polyurethane structural adhesive, its A component is composed of 50% polyol, 15% catalyst, 30% filler and 5% stabilizer; B component is composed of The mass percentage is composed of 50% polymethylene polyphenyl polyisocyanate and 50% hexamethylene diisocyanate.

[0043] The polyol in component A is polyether polyol, and polyether polyol adopts polyoxypropylene diol, polyoxypropylene triol, polyoxypropylene tetraol, poly Composed of tetrahydrofuran diol and propylene oxide-ethylene oxide copolymerized diol.

[0044] The catalyst is two (dodecyl sulfide) dibutyl tin, trimethylene diamine, tetraethylene pentamine, N-methylmorpholine, N-methylimidazole and 1,4-Dimethylpiperazine.

[0045] The filler is talcum powder and diatomaceous earth with a mass ratio of 1:3.

[0046] The stabilizer is fumed white carbon black and polyamide or bentonite with a mass ratio of 3:2.

[0047] The preparation method of comp...

Embodiment 2

[0052] A two-component solvent-free polyurethane structural adhesive with ultra-fast curing at room temperature. The A component is composed of 39.5% polyol, 50% chain extender, 0.5% catalyst, and 10% stabilizer; B component Composed of polymethylene polyphenyl polyisocyanates.

[0053] The polyols in the A component are polyester polyols, and the polyester polyols are polyethylene adipate diol and polypropylene adipate glycol with a power ratio of 1:1:1:1:2. It is composed of ester diol, poly(1,4-butylene adipate) diol, poly(ethylene glycol adipate) diol, and poly(ethylene glycol) phthalate.

[0054] The extender is composed of neopentyl glycol, trimethylolpropane, trimethylolethane, pentaerythritol, and xylitol in a mass ratio of 1:1:1:2:1;

[0055] The catalyst is N-methylmorpholine, N-methylimidazole and 1,4-dimethylpiperazine with a mass ratio of 1:3;

[0056] The stabilizer is bentonite.

[0057] The preparation method of component A is as follows: dehydrate the polyo...

Embodiment 3

[0061] A room temperature ultra-fast curing two-component solvent-free polyurethane structural adhesive. The A component is composed of 90% polyol, 2% chain extender, 5% catalyst, 2% filler and 1% stabilizer. Composition; B component is composed of 60% polymethylene polyphenyl polyisocyanate and 40% hexamethylene diisocyanate by mass percentage.

[0062] The polyols in the A component are polyacrylate polyols, and the polyolefin polyols are hydroxyl-terminated polybutadiene, hydroxyl-terminated polybutadiene resins, hydroxyl-terminated polybutadiene resins with a quality of 1:2:1. ethylene-acrylonitrile or polystyrene polyols;

[0063] The extender is sorbitol;

[0064] The catalyst is zinc isooctanoate and phenylmercuric acetate with a mass ratio of 1:2;

[0065] The filler is titanium dioxide and barium sulfate with a mass ratio of 1:1;

[0066] The stabilizer is fumed white carbon black and bentonite with a mass ratio of 1:1.

[0067] The preparation method of component...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a room temperature super-fast curing double-component solvent-free polyurethane structural adhesive including A and B components; the A component comprises the following components in parts by weight: 50-90 parts of polyols, 0-50 parts of a chain extender, 0.5-15 parts of a catalyst, 0-30 parts of a filler and 5-10 parts of a stabilizer; the B component includes the following two parts: 50-100 parts of polyaryl polymethylene isocyanate and 0-50 parts of hexamethylene diisocyanate. The structural adhesive prepared by the method can be rapidly cured at room temperature.

Description

technical field [0001] The invention relates to an adhesive, more specifically to a room-temperature ultra-fast curing two-component solvent-free polyurethane structural adhesive and a preparation and use method thereof. Background technique [0002] Polyurethane adhesives are widely used in engineering structures, automobile manufacturing and construction industries. Two-component polyurethane structural adhesive has excellent impact resistance, durability, fatigue resistance, low temperature resistance and excellent bonding strength, making it the first polyurethane structural adhesive. Many two-component polyurethane adhesives use solvents, which have a strong odor, are extremely harmful to the health of operators and pollute the environment, and will be replaced by solvent-free polyurethane adhesives; in addition, although there are many fast-curing at room temperature Two-component polyurethane structural adhesive products, but most of these quick-drying adhesives cont...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09J175/04C09J175/06C09J175/08C09J175/14C08G18/76C08G18/73C08G18/69C08G18/66C08G18/65C08G18/42C08G18/48
CPCC08G18/4202C08G18/4816C08G18/4825C08G18/4829C08G18/4837C08G18/4854C08G18/6511C08G18/6588C08G18/664C08G18/6644C08G18/69C08G18/724C08G18/73C08G18/7664C09J175/04C09J175/06C09J175/08C09J175/14
Inventor 石长灿冯亚凯席光辉陈浩李娜杨啸刘雯
Owner WENZHOU INST OF BIOMATERIALS & ENG
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap