Etching solution composition for etching molybdenum/copper/molybdenum or molybdenum alloy/copper/molybdenum alloy three-layer metal wiring structure and application thereof

A metal wiring and molybdenum alloy technology, which is applied in the field of semiconductor metal wiring, can solve the problems of reduced service life of etching solution, unstable concentration of hydrogen peroxide, and inability to maintain etching uniformity and stability, so as to prolong life and stabilize properties , Slow down the effect of decomposition

Active Publication Date: 2021-10-08
TCL CHINA STAR OPTOELECTRONICS TECH CO LTD
View PDF11 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the high content of hydrogen peroxide, the hydrogen peroxide in the etching solution is unstable and the concentration drops rapidly during the etching process, which leads to the inability to maintain the uniformity and stability of the etching when the concentration of copper ions in the etching solution is small, resulting in the corrosion of the etching solution. The life of the etching solution is greatly reduced (about 2000ppm, that is, when the copper ion concentration in the etching solution reaches about 2000ppm, this batch of etching solution can no longer be used, and a new etching solution needs to be replaced)

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0049] This embodiment provides an etching solution composition, its components include by weight percentage: 30wt% hydrogen peroxide, 10wt% glycol, 0.1wt% etching inhibitor, 5wt% chelating agent, 0.1wt% etching additive, 3 wt% pH adjuster and balance water.

[0050] The glycols are ethylene glycol, diethylene glycol and triethylene glycol.

[0051] The pH of the etching solution composition is maintained at 2-6.

[0052] The pH regulator is an organic base.

[0053] The etch inhibitor is a heterocyclic compound containing 1-10 carbon atoms. The heteroatom contained in the heterocyclic compound is oxygen.

[0054] The chelating agent is a compound containing an amino group and a carboxyl group; the chelating agent is iminodiacetic acid, nitrilotriacetic acid and ethylenediaminetetraacetic acid.

[0055] The etching additive is an organic acid.

Embodiment 2

[0057] This embodiment provides an etching solution composition, its components include by weight percentage: 20wt% hydrogen peroxide, 0.1wt% glycol, 5wt% etching inhibitor, 0.1wt% chelating agent, 5wt% etching additive, 0.1 wt% pH adjuster and balance water.

[0058] The dihydric alcohols are propylene glycol, propane-1,2-diol, 1,8-octanediol and cyclopentane-1,2-diol.

[0059] The pH of the etching solution composition is maintained at 3-5.

[0060] The pH regulator is an inorganic base and a basic salt.

[0061] The etch inhibitor is a heterocyclic compound containing 1-10 carbon atoms. The heteroatoms contained in the heterocyclic compound are sulfur and nitrogen.

[0062] The chelating agent is a compound containing amino and carboxyl groups. The chelating agent is diethylenetriaminepentaacetic acid, aminotrimethylenephosphonic acid and 1-hydroxyethylene-1,1-diphosphoric acid.

[0063] The etching additives are inorganic acids and phosphates. Described phosphate is ...

Embodiment 3

[0065] This embodiment provides a kind of etchant composition, and its component comprises by weight percent: 25wt% hydrogen peroxide, 5.5wt% glycol, 2.5wt% etching inhibitor, 3wt% chelating agent, 2.5wt% etching additive , 1.5wt% pH regulator and the balance of water.

[0066] The dihydric alcohols are ethylene glycol, 1,2-propanediol, 1,4-butanediol and cyclohexane-1,4-diol.

[0067] The pH of the etching solution composition is maintained at 3-6.

[0068] The pH regulator is a basic salt.

[0069] The etch inhibitor is a heterocyclic compound containing 1-10 carbon atoms. The heteroatoms contained in the heterocyclic compound are oxygen and nitrogen.

[0070] The chelating agent is a compound containing amino and carboxyl groups. The chelating agent is iminodiacetic acid, ethylenediaminetetraacetic acid and ethylenediaminetetramethylphosphoric acid.

[0071] The etching additive is phosphate. The phosphates are monoammonium phosphate, triammonium phosphate and disodiu...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The application discloses an etching solution composition capable of etching molybdenum / copper / molybdenum or molybdenum alloy / copper / molybdenum alloy three-layer metal wiring structure and its application. The etching solution composition components include hydrogen peroxide, glycol, etch inhibitor, chelating agent, etching additive, pH regulator and water; the glycol is ethylene glycol, propylene glycol, diethylene glycol, propane ‑1,2‑diol, triethylene glycol, 1,2‑propanediol, 1,3‑propanediol, 1,4‑butanediol, 1,5‑pentanediol, 1,6‑hexanediol, 1, 7‑Heptanediol, 1,8‑octanediol, 1,9‑nonanediol, 1,10‑decanediol, cyclopentane‑1,2‑diol and cyclohexane‑1,4‑diol one or more of them. The etching solution of the present invention not only slows down the decomposition of hydrogen peroxide, but also prolongs the life of the etching solution to 3000-4000ppm, greatly reduces the cost of the etching solution in the manufacturing process, and improves the safety factor of the etching solution.

Description

technical field [0001] The present application relates to the technical field of semiconductor metal wiring, in particular to the technical field of metal wiring etching, in particular to an etchant composition for etching a three-layer metal wiring structure of molybdenum / copper / molybdenum or molybdenum alloy / copper / molybdenum alloy and its application. Background technique [0002] The process of forming metal wiring on the semiconductor array substrate usually includes: sputtering (Sputter) film forming process, photoresist or photoresist coating and development process, wet etching process for forming metal wiring and metal wiring pattern Post-chem removal of unwanted photoresist or photoresist stripping process. [0003] For different metal wiring structures, metal wiring upper and lower layer structures, and different array substrate manufacturing processes, the requirements for etching properties of the etchant are also different. When the layer below the metal wiri...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C23F1/44
CPCC23F1/44C23F1/18C23F1/26H05K3/067H05K2201/0361H05K2203/0789C23F1/14H01L21/306H01L21/32134C23F1/10H01L21/30604
Inventor 刘净
Owner TCL CHINA STAR OPTOELECTRONICS TECH CO LTD