Anti-dazzle film special for anti-dazzle glass

An anti-glare glass and anti-glare technology, applied in coatings, epoxy resin coatings, polycarbonate coatings, etc., can solve the problem of low adhesion of anti-glare films, poor scratch resistance, and easy to appear on the surface Scratches and other problems, achieve the effect of reducing dazzling refraction and scattering, excellent adhesion and weather resistance, and improving mechanical properties

Inactive Publication Date: 2015-11-11
ANHUI HERUN SPECIAL GLASS CO LTD
View PDF3 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Coating glass is an important way to prepare anti-glare glass, but the existing anti-glare film does not have very high adhesion to the substrate, it is easy to fall off during use, and its scratch resistance is not very good. During use, the surface is prone to scratches and loses the anti-glare effect

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] A special anti-glare coating film for anti-glare glass proposed by the present invention, its raw materials include the following components by weight: 35 parts of epoxy acrylate oligomers, 10 parts of polyurethane acrylate oligomers, 25 parts of polycarbonate, 10 parts of styrene, 25 parts of methyl methacrylate, 8 parts of trimethylolpropane triacrylate, 5 parts of polyethylene glycol, 1 part of tricumyl phosphate, 10 parts of nano titanium dioxide, nano silicon dioxide 1 part, 5 parts of aluminum stearate, 0.5 parts of fluorine-doped tin oxide, 15 parts of ethyl acetate, 5 parts of glycerol, 20 parts of ethylene glycol, 5 parts of toluene, 35 parts of m-trifluorotoluene, silane coupling 2.5 parts of agent, 2 parts of sodium dodecylbenzenesulfonate, 3.5 parts of 1-hydroxycyclohexyl phenyl ketone, 2 parts of benzophenone, 2.8 parts of amino resin, and 2 parts of leveling agent.

Embodiment 2

[0020] A special anti-glare coating film for anti-glare glass proposed by the present invention, its raw materials include the following components by weight: 20 parts of epoxy acrylate oligomers, 25 parts of polyurethane acrylate oligomers, 10 parts of polycarbonate, 25 parts of styrene, 5 parts of methyl methacrylate, 20 parts of trimethylolpropane triacrylate, 1 part of polyethylene glycol, 10 parts of tricumyl phosphate, 2 parts of nano titanium dioxide, nano silicon dioxide 3.5 parts, 1 part of aluminum stearate, 2 parts of fluorine-doped tin oxide, 5 parts of ethyl acetate, 20 parts of glycerol, 8 parts of ethylene glycol, 15 parts of toluene, 20 parts of m-trifluorotoluene, silane coupling 1 part of agent, 5 parts of sodium dodecylbenzenesulfonate, 1 part of 1-hydroxycyclohexyl phenyl ketone, 5 parts of benzophenone, 1 part of amino resin, 2 parts of dispersant, and 1.5 parts of defoamer.

Embodiment 3

[0022] A kind of special anti-glare coating film for anti-glare glass proposed by the present invention, its raw material comprises the following components by weight: 29 parts of epoxy acrylate oligomers, 20 parts of polyurethane acrylate oligomers, 19 parts of polycarbonate, 20 parts of styrene, 14 parts of methyl methacrylate, 16 parts of trimethylolpropane triacrylate, 3.2 parts of polyethylene glycol, 7.6 parts of tricumyl phosphate, 5.8 parts of nano titanium dioxide, nano silicon dioxide 2.7 parts, 3.2 parts of aluminum stearate, 1.3 parts of fluorine-doped tin oxide, 10 parts of ethyl acetate, 15 parts of glycerol, 16 parts of ethylene glycol, 12 parts of toluene, 30 parts of m-trifluorotoluene, coupling agent 0.3 parts of KH-5700, 0.5 parts of silane coupling agent KH5600, 1 part of silane coupling agent KH-5501, 0.2 parts of vinyl-tris(2-methoxyethoxy) silane, 3.8 parts of sodium dodecylbenzenesulfonate part, 2.5 parts of 1-hydroxycyclohexyl phenyl ketone, 3.8 parts ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
The average particle sizeaaaaaaaaaa
The average particle sizeaaaaaaaaaa
The average particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses an anti-dazzle film special for anti-dazzle glass. The anti-dazzle film comprises epoxy acrylate oligomer, urethane acrylate oligomer, polycarbonate, styrene, methyl methacrylate, trimethylolpropane triacrylate, polyethylene glycol, tri-isopropylphenyl phosphate, nano-titanium dioxide, nanosilicon dioxide, aluminum stearate, fluorine-doped tin oxide, ethyl acetate, glycerol, ethanediol, toluene, 1,3-bis(trifluoromethyl)-benzene, silane coupling agent, sodium dodecyl benzene sulfonate, 1-hydroxyl cyclohexyl phenyl ketone, benzophenone, amino resin and auxiliaries. The anti-dazzle film special for anti-dazzle glass is high in adhesion with a substrate, does not drop easily in the using process and is good in scratch resistance and high in transparency, and the yield of the anti-dazzle glass prepared from the anti-dazzle film is high.

Description

technical field [0001] The invention relates to the technical field of anti-glare glass, in particular to a special anti-glare coating film for anti-glare glass. Background technique [0002] Glare is a kind of serious light pollution, which will cause the decline of visual functions such as contrast perception, vision and recognition speed of the eyes, and also affect people's emotions, making people dizzy and upset, loss of appetite, irritability, depression, physical fatigue, etc. Seriously interfere with and hinder people's normal life. As for the control of glare pollution, there are no clear regulations and standards at home and abroad. Therefore, in order to maintain people's visual health and improve labor efficiency, the protection of glare is particularly important. [0003] Anti-glare glass can reduce the interference of ambient light, reduce the reflection of the screen, improve the viewing angle and brightness of the display screen, make the image clearer, the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D163/10C09D175/14C09D169/00C09D7/12
Inventor 凌卫平
Owner ANHUI HERUN SPECIAL GLASS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com