Enhanced metal ceramic abrasion-resistant composite material and preparation method thereof

A cermet and composite material technology, applied in the field of wear-resistant composite materials, can solve the problems of short life and large maintenance, and achieve the effects of low cost, good thermal shock resistance and outstanding wear resistance

Inactive Publication Date: 2015-11-25
NANTONG GAOXIN ANTIWEAR MATERIALS TECH CO LTD
View PDF5 Cites 32 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Plastic polymer materials are not as good as ceramic composite materials in terms of temperature resistance, climate change resistance, and wear resistance, and have defects such as short life and large maintenance. This invention proposes a new technical solution for ceramic composite materials.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] An enhanced cermet wear-resistant composite material, comprising the following components in parts by mass:

[0024] 25 parts of nano-molybdenum carbide, 15 parts of nano-ceramic powder, 10 parts of glass fiber, 5 parts of cobalt, 10 parts of chromium, 10 parts of titanium carbonitride, 1 part of zirconia, 3 parts of silicon oxide, 8 parts of cerium oxide, and 1 part of aluminum oxide - parts, 5 parts of niobium carbide, 5 parts of silicon carbide, 1 part of vanadium carbide, 4 parts of copper, 1 part of titanium powder, 1 part of coupling agent, 1 part of antistatic agent, and 1 part of curing agent.

[0025] The preparation method of the above-mentioned enhanced cermet wear-resistant composite material comprises the following steps:

[0026] (1) Batch and mix each component according to the parts by mass, and the particle size of each powder is 500 mesh;

[0027] (2) Put the above powder into the ball mill, and then inject water, the ratio of water injection weight t...

Embodiment 2

[0031] An enhanced cermet wear-resistant composite material, comprising the following components in parts by mass:

[0032] 35 parts of nano molybdenum carbide, 25 parts of nano ceramic powder, 15 parts of glass fiber, 10 parts of cobalt, 15 parts of chromium, 15 parts of titanium carbonitride, 3 parts of zirconia, 5 parts of silicon oxide, 10 parts of cerium oxide, 3 parts of aluminum oxide 10 parts of niobium carbide, 15 parts of silicon carbide, 3 parts of vanadium carbide, 9 parts of copper, 5 parts of titanium powder, 5 parts of coupling agent, 3 parts of antistatic agent, and 3 parts of curing agent.

[0033] The preparation method of the above-mentioned enhanced cermet wear-resistant composite material comprises the following steps:

[0034] (1) Batch and mix each component according to the parts by mass, and the particle size of each powder is 800 mesh;

[0035] (2) Put the above powder into the ball mill, and then inject water, the ratio of water injection weight to ...

Embodiment 3

[0039] An enhanced cermet wear-resistant composite material, comprising the following components in parts by mass:

[0040] 27 parts of nano molybdenum carbide, 18 parts of nano ceramic powder, 11 parts of glass fiber, 6 parts of cobalt, 12 parts of chromium, 11 parts of titanium carbonitride, 1.5 parts of zirconia, 3.5 parts of silicon oxide, 8.5 parts of cerium oxide, 1.5 parts of aluminum oxide 7 parts of niobium carbide, 7 parts of silicon carbide, 1.5 parts of vanadium carbide, 6 parts of copper, 2 parts of titanium powder, 2 parts of coupling agent, 1.5 parts of antistatic agent, and 1.5 parts of curing agent.

[0041] The preparation method of the above-mentioned enhanced cermet wear-resistant composite material comprises the following steps:

[0042] (1) Batch and mix each component according to the parts by mass, and the particle size of each powder is 650 mesh;

[0043] (2) Put the above powder into the ball mill, and then inject water, the ratio of water injection ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
flexural strengthaaaaaaaaaa
particle sizeaaaaaaaaaa
Rockwell hardnessaaaaaaaaaa
Login to view more

Abstract

The invention discloses an enhanced metal ceramic abrasion-resistant composite material and a preparation method thereof. The composite material is composed of, by mass, 25-35 parts of nano molybdenum carbide, 15-25 parts of nano ceramic powder, 10-15 parts of glass fiber, 5-10 parts of cobalt, 10-15 parts of chrome, 10-15 parts of titanium carbonitride, 1-3 parts of zirconium oxide, 3-5 parts of silicon oxide, 8-10 parts of cerium oxide, 1-3 parts of aluminium oxide, 5-10 parts of niobium carbide, 5-15 parts of silicon carbide, 1-3 parts of vanadium carbide, 4-9 parts of copper, 1-5 parts of titanium powder, 1-5 parts of coupling agents, 1-3 parts of antistatic agents and 1-3 parts of curing agents. The preparation method of the enhanced metal ceramic abrasion-resistant composite material just comprises mixing, drying, sintering and cooling. The metal ceramic composite material has good properties that the bending resistant strength is up to 2500 MPa and the Rockwell hardness is up to 93; in addition, the metal ceramic composite material also has good properties of abrasion resistance and high temperature resistance; the preparation method is simple and feasible and suitable for application and popularization on a large scale.

Description

technical field [0001] The invention belongs to the technical field of wear-resistant composite materials, and in particular relates to a reinforced cermet wear-resistant composite material and a preparation method thereof. Background technique [0002] Cermet is a composite material composed of ceramic hard phase and metal or alloy binder phase. Cermet not only maintains the characteristics of high strength, high hardness, wear resistance, high temperature resistance, oxidation resistance and chemical stability of ceramics, but also Has good metal toughness and plasticity. [0003] Cermets have gone through three generations so far. The first generation was during the "World War II", Germany produced cermets with Ni bonded TiC; The wettability of other carbides improves the toughness of the material; the third generation of cermets introduces nitrides into the hard phase of the alloy and changes the single phase into a composite phase. The binder phase is also improved by...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C22C30/00C22C1/05
CPCC22C1/05C22C29/02
Inventor 钱兵孙书刚
Owner NANTONG GAOXIN ANTIWEAR MATERIALS TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap