Heat-resisting powder coating for auto vent pipe and preparing method thereof

A technology for automotive exhaust and powder coatings, applied in powder coatings, anti-corrosion coatings, polyester coatings, etc., can solve the problems of high cost and popularization, and achieve the effects of improving storage stability, low curing temperature, and improving compatibility

Inactive Publication Date: 2016-09-21
合肥燕美新材料科技有限公司
View PDF3 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although the existing high-temperature-resistant powder coatings are more environmentally friendly than oil-based coatings, their popularization is limited due to their high cost and high-temperature curing (curing conditions are at least 230°C×20 minutes)

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Heat-resisting powder coating for auto vent pipe and preparing method thereof
  • Heat-resisting powder coating for auto vent pipe and preparing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0020] A heat-resistant powder coating for automobile exhaust pipes, prepared from the following components by weight (kg): silicone modified epoxy resin 15, o-cresol novolac epoxy resin 85, hydroxyl polyester resin 12, Polyisocyanate 14, polyester polyol 11, silane coupling agent 2, antioxidant 1010 1, EPDM rubber 5, silicon carbide 4, boron nitride 1, mica powder 18, 2,6-tertiary butyl -4-methylphenol 2.5, double dodecyl alcohol ester 0.6, superfine barium sulfate 17, carbon black 9, benzoin 0.6, modification additive 2,

[0021] Among them, the modified auxiliary agent is made of the following components by weight (kg): polyvinyl alcohol superfine powder 25, zinc borate 1.5, aluminum oxide C6, magnesium oxide 3-4, castor oil 3, boron nitride 1.5, gas phase two Silicon oxide 5, xylene 35, alkoxy diol 4, alkoxy triol 4, dimethylolpropionic acid 5, polysiloxane 3, p-toluenesulfonic acid 0.3, caprolactone 6, di Dibutyltin laurate 0.3, the preparation method of modified additiv...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides heat-resisting powder coating for an auto vent pipe. The heat-resisting powder coating is prepared from, by weight, 10-20 parts of organosilicon-modified epoxy resin, 80-90 parts of o-cresol formaldehyde epoxy resin, 10-20 parts of hydroxyl polyester resin, 10-15 parts of polyisocyanate, 10-12 parts of polyester polyol, 1-2 parts of silane coupling agent, 1-2 parts of antioxidant 1010, 4-6 parts of ethylene propylene diene monomer, 3-5 parts of silicon carbide, 1-2 parts of boron nitride, 15-20 parts of mica powder, 2-3 parts of 2,6-tert-butyl-4-methylphenol, 0.5-1.0 part of 2,2,4-trimethyl-1,3-pentanediol monoisobutyrate, 15-18 parts of superfine barium sulfate, 8-10 parts of carbon black, 0.5-0.7 part of benzoin and 1-2 parts of performance additive. The coating is high in heat resistance, low in curing temperature, short in curing time, high in adhesive force and resistant to acid and alkali, and can be applied to coating of the auto vent pipe, and a coating film is high in levelling property and good in appearance.

Description

technical field [0001] The invention belongs to the field of coatings, in particular to a heat-resistant powder coating for automobile exhaust pipes and a preparation method thereof. Background technique [0002] With the advancement of modern science and technology and the development of modern industry, the problem of environmental pollution has become increasingly prominent, which poses a great threat to human beings themselves and the environment on which human beings depend. Traditional coatings will produce a large amount of toxic and harmful waste gas and waste water during the manufacturing process or during the construction process, which will pollute the environment, air and water resources, especially solvent-based coatings, which will release Volatile organic compounds (VOC) into the atmosphere, its amount has reached more than 50%, causing serious secondary pollution. This problem has attracted the attention of many industrial countries. [0003] As a kind of ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D163/04C09D167/00C09D5/03C09D5/08C09D7/12
CPCC08L2201/08C08L2205/02C08L2205/025C08L2205/035C09D5/03C09D5/033C09D5/08C09D163/04C08L63/00C08L67/00C08L23/16C08K13/06C08K9/06C08K2003/222C08K3/36C08K3/34C08K2003/3045
Inventor 陈俊刘学涛赵遵刚霍柏林李正孙红兴
Owner 合肥燕美新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products