A kind of water-based adhesive for automobile filter and preparation method thereof

A water-based adhesive and filter technology, applied in the direction of adhesive types, ester copolymer adhesives, polymer adhesive additives, etc., can solve the problems of slow drying speed, poor antifreeze, and low temperature resistance , achieve the effect of fast drying, strong antifreeze and improved adhesion

Active Publication Date: 2018-09-14
佛山市豹王滤芯制造有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the disadvantages of water-based adhesives mainly include slow drying speed, poor water resistance, poor freeze resistance, and high temperature resistance, and often need to be modified. For example, the Chinese patent application "a water-based polyurethane adhesive" with the publication number CN 102965060 B uses 2 , 6-toluene diisocyanate, 1,4-butylene adipate, diethylene glycol, and dimethylol butyric acid are used as raw materials to prepare prepolymers, and trimethylolpropane and epoxy resin are added Carry out cross-linking, add triethylamine for neutralization reaction to generate salt, add butyl acrylate and water for emulsification, add an appropriate amount of potassium persulfate to polymerize butyl acrylate, and obtain a modified water-based polyurethane adhesive. After the mixture is formed into a film, it has good thermal stability, chemical resistance and mechanical properties

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of water-based adhesive for automobile filter and preparation method thereof
  • A kind of water-based adhesive for automobile filter and preparation method thereof
  • A kind of water-based adhesive for automobile filter and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] Embodiment 1 Modified polyetheramine fiber preparation

[0034] The preparation raw material of modified polyetheramine fiber comprises the component of following parts by weight:

[0035] 100 parts of polyetheramine D-230, 150 parts of glyceraldehyde, 5 parts of sodium lauryl sulfate, 15 parts of N,N-methylenebisacrylamide, 5 parts of potassium persulfate, and an appropriate amount of glacial acetic acid.

[0036]Preparation:

[0037] Dissolve polyetheramine D-230 in water to make an aqueous solution with a mass concentration of 100g / L, add sodium lauryl sulfate, stir evenly, heat up to 60°C, add glyceraldehyde, and add appropriate amount of glacial acetic acid to make the pH of the system The value is 3, the solution is fully emulsified, after standing for 10 minutes, add the pre-dissolved concentration of 10g / L N, N-methylenebisacrylamide aqueous solution and 5g / L potassium persulfate aqueous solution, and continue the reaction for 2h, and the reaction Liquid cooli...

Embodiment 2

[0038] Embodiment 2 Acrylic acid-butyl acrylate-styrene copolymer emulsion preparation

[0039] (1) Weigh the polymerized monomer acrylic acid, butyl acrylate and styrene respectively after decompression refining, and mix well. The weight ratio of the acrylic acid, butyl acrylate and styrene is 3.2:4.4:0.9, and then add 2wt % initiator azobisisobutyronitrile (AIBN), mix evenly, then add an appropriate amount of n-butanol to prepare a mixed solution with a solid content of more than 60%, for subsequent use;

[0040] (2) Get 50mL n-butanol and place it in the reactor, heat it up to the solvent reflux temperature, slowly add the mixed solution prepared in step (1) dropwise under uniform stirring, the volume ratio of the mixed solution and n-butanol is 2 : 1, the rate of addition is 0.8mL / min, reflux reaction at 100°C for 6h, after the reaction is over, cool down to 60°C, add ammonia water dropwise under stirring, until the pH value of the system reaches 8, dilute with water, and ...

Embodiment 3-5 and comparative example 1-4

[0041] Embodiment 3-5 and comparative example 1-4 water-based adhesive preparation

[0042] Embodiment 3-5 and comparative example 1-4 water-based binder comprise components and parts by weight thereof shown in the table below:

[0043]

[0044]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
peel strengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to a waterborne adhesive for an automobile filter and a preparation method of the waterborne adhesive. The adhesive comprises the following components in parts by weight: 40-80 parts of hydrophilic polymer emulsion, 10-20 parts of enhancer, 1-3 parts of stabilizer, 1-4 parts of thixotropic agent, 1-2 parts of silyl ether, 20-30 parts of glycerin, 0.05-1 part of zinc oxide and1-3 parts of sodium dodecyl sulfate. The adhesive is curable at normal temperature, high in drying speed, good in water resistance, high in bonding strength, stable in property, few in influences from temperature and humidity, free of releasing solvents, green, environment-friendly, nontoxic and safe in use.

Description

technical field [0001] The invention relates to the technical field of adhesives, in particular to a water-based adhesive for automobile filters and a preparation method thereof. Background technique [0002] The filter is one of the key components to ensure the durability and reliability of the engine. The engine has three filters of air, oil and fuel, generally called "three filters", plus the air conditioning filter, commonly known as "four filters", which are respectively responsible for the lubrication system, the medium of the combustion system, the engine intake system, and the cabin. Filtration of the air circulation system. The air filter is mainly used in pneumatic machinery, internal combustion machinery and other fields. Its function is to provide clean air for these mechanical equipment, so as to prevent these mechanical equipment from inhaling air with impurity particles during work and increasing the probability of abrasion and damage. Automobile engines are...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09J133/08C09J11/04C09J11/06C09J11/08C08F220/18C08F220/06C08F212/08C08F283/00C08F222/38
CPCC08F220/18C08F220/1804C08F283/00C08K2003/2296C08L2201/08C08L2205/035C08L2205/16C09J11/04C09J11/06C09J11/08C09J133/064C08L51/08C08L79/02C08L91/00C08K13/02C08K3/22C08K5/053C08K5/526C08F222/385C08F220/06C08F212/08
Inventor 杨广博莫基
Owner 佛山市豹王滤芯制造有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com