Potassium titanyl phosphate film negative electrode material as well as preparation method and application thereof

A technology of potassium titanyl phosphate and negative electrode material, which is applied in the fields of nanotechnology, chemical instruments and methods, and phosphorus compounds for materials and surface science. Uneven mixing and other problems, to achieve the effect of favorable electron transport, excellent cycle stability and low cost

Active Publication Date: 2020-04-17
WUHAN UNIV OF TECH
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In the existing technology for preparing potassium titanyl phosphate, the potassium titanyl phosphate prepared by liquid phase co-precipitation, ion implantation or ion exchange is used in the field of nonlinear optical materials, which is not suitable for the battery field; Potassium titanyl phosphate powder material is synthesized by solid phase method for use in the battery field. This preparation method is prepared through two steps of grinding and high-temperature solid-state reaction. During the grinding process, the raw materials may be mixed unevenly; in addition, the high-temperature reaction consumes a lot of energy and may damage the material. The prepared powder needs to be mixed with additives and then coated on the current collector to obtain an electrode, which reduces the mass fraction of the electrode active material, thereby limiting the improvement of its electrochemical performance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Potassium titanyl phosphate film negative electrode material as well as preparation method and application thereof
  • Potassium titanyl phosphate film negative electrode material as well as preparation method and application thereof
  • Potassium titanyl phosphate film negative electrode material as well as preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] This example shows a preparation method of potassium titanyl phosphate thin film negative electrode material.

[0032] Potassium titanyl phosphate film is synthesized by a one-step hydrothermal method, including the following steps:

[0033] (1) 50μm 3.5*3.5cm 2 Polish the titanium sheet with 360-mesh sandpaper to clean the oxide layer on its surface; (2) ultrasonically clean it with hydrochloric acid, acetone and absolute ethanol for 15 minutes each; (3) mix potassium dihydrogen phosphate and deionized water evenly to obtain 2mol / L (4) place the titanium sheet and the above solution in an autoclave with a polytetrafluoroethylene liner substrate, and conduct a hydrothermal reaction at 220°C for 24 hours; (5) put the above step (4) after the hydrothermal reaction for a long The titanium sheet with the potassium titanyl phosphate film is taken out, rinsed with deionized water, and dried in an oven to finally prepare a binder-free potassium titanyl phosphate negative elec...

Embodiment 2

[0036] This example shows a sodium-ion battery in which a potassium titanyl phosphate film is used as the negative electrode of the binder-free sodium-ion battery.

[0037] The potassium titanyl phosphate thin film obtained in embodiment 1 is cut into 1*1cm 2 The square electrode sheet is used as the negative electrode material of the sodium ion battery, and the counter electrode and the reference electrode of the sodium ion battery are metallic sodium.

[0038] The formula of the electrolyte consists of: the solvent is Diglyme (diglyme); the electrolyte sodium salt is NaPF 6 , the concentration of the substance in the electrolyte is 1mol / L.

[0039] Assemble the above-mentioned potassium titanyl phosphate negative electrode sheet, electrolyte, metal sodium and others such as glass fiber diaphragm, stainless steel gasket, spring and battery casing into a 2032-type button battery.

[0040]Carry out cyclic voltammetry and constant current charge and discharge tests on the batt...

Embodiment 3

[0042] This example shows a potassium titanyl phosphate thin film used as the negative electrode of the binder-free potassium ion battery.

[0043] The potassium titanyl phosphate thin film obtained in embodiment 1 is cut into 1*1cm 2 The square electrode sheet is used as the negative electrode material of the potassium ion battery, and the counter electrode and the reference electrode of the potassium ion battery are potassium metal.

[0044] The composition of the electrolyte is as follows: the solvent is EC (ethylene carbonate) / PC (propylene carbonate); the electrolyte potassium salt is KPF 6 , the concentration of the substance in the electrolyte is 1mol / L.

[0045] Assemble the above-mentioned potassium titanyl phosphate negative electrode sheet, electrolyte, metal potassium foil and others such as glass fiber diaphragm, stainless steel gasket, spring and battery casing into a 2032-type button battery.

[0046] Carry out cyclic voltammetry and constant current charge an...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the technical field of sodium / potassium ion batteries. The invention particularly relates to a potassium titanyl phosphate film negative electrode material as well as a preparation method and application thereof. A titanium substrate is used as a current collector; a potassium titanyl phosphate (with the chemical formula of KTiOPO4) film growing on the titanium substrate serves as an active material, the mass fraction of the active material is 100%, the potassium titanyl phosphate film has excellent flexibility, potassium titanyl phosphate nanowires form an almond-shaped microstructure, and gaps exist between the nanowires. The method is simple in process preparation, high in repeatability, low in energy consumption and low in cost, and has important significance in research of a flexible sodium / potassium ion battery negative electrode material; meanwhile, large-area uniform growth of the potassium titanyl phosphate film on the titanium substrate can be achieved, and industrial application is facilitated. In addition, the material grown in situ on the metal substrate by the one-step hydrothermal method can also be applied to the synthesis of other materials.

Description

technical field [0001] The invention belongs to the technical field of sodium / potassium ion batteries, and in particular relates to a potassium titanyl phosphate film negative electrode material and a preparation method thereof, which can be used as the negative electrode material of sodium / potassium ion batteries. Background technique [0002] Metal sodium and potassium are considered to be the most promising batteries to replace lithium-ion batteries in our lives due to their abundant reserves, low cost, and similar physical and chemical properties and energy storage mechanisms to lithium. one. due to sodium ions and potassium ions The radius is larger than that of Li-ion The radius of the electrode is large, and its intercalation / extraction usually causes changes in the structure of the electrode material, which in turn leads to problems such as material lattice strain, material structure stability, and poor cycle life. Therefore, most of the existing lithium-ion ba...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): H01M4/58H01M10/0525H01M10/054C01B25/45B82Y30/00
CPCB82Y30/00C01B25/45H01M4/5825H01M10/0525H01M10/054Y02E60/10
Inventor 刘金平刘文燚易成军刘雯聪陈瑶郭雪丽
Owner WUHAN UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com