Preparation method of super-hydrophobic coating with high light transmittance and high haze

A technology of super-hydrophobic coating and high light transmittance, which is applied in coatings, fireproof coatings, etc., and can solve the problems that it is difficult to meet high haze, high light transmittance, low haze, and failure to reach a super-hydrophobic state at the same time. Achieve the effect of simple preparation method, easy operation and high light transmittance

Active Publication Date: 2021-09-03
CHANGZHOU UNIV
View PDF12 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Then the porous membrane is perfused with modified silicone oil to prepare a hydrophobic star-shaped polymer porous membrane. Its light transmittance is close to that of glass, but its hydrophobicity is less than 150°, which does not reach the superhydrophobic state.
And it does not involve research on haze issues
Generally, materials with high light transmittance have low haze, and it is difficult to meet the effects of high haze and high light transmittance at the same time

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of super-hydrophobic coating with high light transmittance and high haze
  • Preparation method of super-hydrophobic coating with high light transmittance and high haze
  • Preparation method of super-hydrophobic coating with high light transmittance and high haze

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] (1) Synthesis of star copolymer POSS-PS

[0021] 0.42g of octachloropropyl cage silsesquioxane, 0.04g of cuprous chloride and 0.2g of 2,2'-bipyridine, 9.2ml of styrene, 3ml of N,N-dimethylamide , added to a Schlenk bottle, and reacted at 110° C. for 24 hours by atom transfer radical polymerization (ATRP) to synthesize a star-shaped copolymer POSS-PS.

[0022] (2) Synthesis of room temperature curing silicone rubber

[0023] Mix 10 g of hydroxyl-terminated polysiloxane with 1 g evenly to obtain room temperature curing silicone rubber.

[0024] (3) prepare superhydrophobic coating;

[0025] Weigh 20mg of star copolymer POSS-PS star copolymer and dissolve in 1ml of dichloromethane (solubility is 20mg / ml), 10mg of room temperature curing silicone rubber is dissolved in 1ml of dichloromethane, ultrasonically until dissolved, the two solutions Mix evenly by volume 1:1 to obtain a mixed solution. The glass substrate is placed in a n-hexane coagulation bath, and then the ab...

Embodiment 2

[0044] (1) Synthesis of star copolymer POSS-PS

[0045] Mix 0.42g of octachloropropyl cage silsesquioxane, 0.04g of cuprous chloride and 0.2g of 2,2'-bipyridyl, 6.9ml of styrene, 2ml of N,N-dimethylamide , added to a Schlenk bottle, and reacted at 110° C. for 24 hours by atom transfer radical polymerization (ATRP) to synthesize a star copolymer POSS-PS.

[0046] (2) synthetic room temperature curing silicone rubber, with embodiment 1;

[0047] (3) Prepare super-hydrophobic coating, same as embodiment 1.

Embodiment 3

[0053] (1) Synthesis of star copolymer POSS-PS

[0054] Mix 0.42g of octachloropropyl cage silsesquioxane, 0.04g of cuprous chloride and 0.2g of 2,2'-bipyridine, 4.6ml of styrene, 1.6ml of N,N-dimethyl The amide was added into a Schlenk bottle, and reacted at 110° C. for 24 hours by atom transfer radical polymerization (ATRP) to synthesize a star-shaped copolymer POSS-PS.

[0055] (2) synthetic room temperature curing silicone rubber, with embodiment 1;

[0056] (3) Prepare super-hydrophobic coating, same as embodiment 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
concentrationaaaaaaaaaa
Login to View More

Abstract

The invention relates to the field of super-hydrophobic materials, in particular to a preparation method of a super-hydrophobic coating with high light transmittance and high haze. The star copolymer POSS-PS is synthesized by taking octa (chloropropyl) polyhedral oligomeric silsesquioxane, styrene, 2-2 bipyridine and cuprous chloride as raw materials through an atom transfer radical polymerization method; the star copolymer POSS-PS and prepared room-temperature cured silicone rubber are dissolved in a solvent through a non-solvent phase separation (NIPS) method, and mixed, and the mixture is poured into a non-solvent coagulating bath containing a matrix to obtain the super-hydrophobic coating. The preparation method is simple and easy to operate, and the prepared coating has the characteristics of superhydrophobicity, adhesion prevention, self-cleaning, high temperature resistance, high light transmittance, high haze and the like.

Description

technical field [0001] The invention relates to the field of superhydrophobic materials, in particular to a method for preparing a superhydrophobic coating with high light transmittance and high haze. Background technique [0002] Inspired by the fact that the cluster structure on the surface of the lotus leaf is good for locking air and preventing water from wetting the surface, superhydrophobic materials with good wettability with a contact angle exceeding 150° can be prepared. The preparation of superhydrophobic materials with unique microstructures is diverse, including etching, templates, femtosecond laser etching, photolithography, casting, in situ polymerization, electrochemical methods, self-assembly methods, electrospinning silk method and spin coating method, etc. It is widely used in self-cleaning, anti-corrosion, anti-icing, battery interference shielding, self-repairing, droplet manipulation, pipeline transportation, oil-water separation, biomedical and other f...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D153/00C09D183/08C09D5/00C03C17/30
CPCC09D153/00C09D183/08C09D5/00C09D5/18C03C17/30C03C17/006C03C17/001C03C2217/40C03C2217/70C03C2218/111C08L2201/08C08L2201/10C08L83/08
Inventor 张洪文李欣顾钦天胡建杨丽吕程程买重阳姜彦
Owner CHANGZHOU UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com