Silver-based circuit board chemically plated with nickel, palladium and gold and preparation method of silver-based circuit board

A technology of electroless nickel plating and electroless gold plating, applied in liquid chemical plating, metal material coating process, coating, etc. Use and other problems to achieve the effect of high sensitivity, long life and reduced thickness

Active Publication Date: 2019-11-19
珠海联鼎化工设备有限公司
View PDF6 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] At present, the commonly used electroless plating substrate is copper base, but the copper base after microetching treatment is easily polluted and oxidized by the environment.
At the same time, the use of copper-based substrates generally requires a thicker nickel layer and palladium layer to prevent the oxidation of the copper-based substrate and prevent the diffusion of copper ions to the gold layer and migration to the surface of the circuit board, causing poor solderability of the product.
Furthermore, considering factors such as its performance and production cost, many people choose the electroless nickel plating process instead of the electroless gold plating process. However, the electroless nickel plating pro

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Silver-based circuit board chemically plated with nickel, palladium and gold and preparation method of silver-based circuit board
  • Silver-based circuit board chemically plated with nickel, palladium and gold and preparation method of silver-based circuit board

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0047] Cleaning: Put the silver-based substrate into a super water tank filled with ultra-pure water, immerse the silver-based substrate, apply slight vibration at room temperature, and treat for 10 minutes to remove dust and other impurities on the surface of the silver-based substrate. Then put the product into a mixed solution of 3% sodium dodecylsulfonate and 20g / L sodium hydroxide for ultrasonic vibration degreasing treatment; use 50g / L dodecyl ammonium chloride and 30mL / L The chloric acid mixture is ultrasonically oscillated for deoxidation treatment.

[0048] Micro-etching treatment: place the above-mentioned cleaned silver-based substrate in a mixed solution containing 30mL / L of chloric acid and 100g / L of hydrogen peroxide for micro-etching treatment. The treatment temperature is 25°C, and the time is 2min. After treatment, the surface of the silver layer is relatively flat and smooth; the micro-etching pore size is relatively uniform, and the surface roughness is smal...

Embodiment 2

[0059] Cleaning: Put the silver-based substrate into a super water tank filled with ultra-pure water, immerse the silver-based substrate, apply slight vibration at room temperature, and treat for 10 minutes to remove dust and other impurities on the surface of the silver-based substrate. Then put the product into a mixed solution of sodium dodecylsulfonate with a mass fraction of 4% and 25g / L sodium hydroxide for ultrasonic vibration degreasing treatment; use 60g / L lauryl ammonium chloride and 30mL / L The methanesulfonic acid mixture is ultrasonically oscillated for deoxidation treatment.

[0060] Microetching treatment: place the above-mentioned cleaned silver-based substrate in a mixed solution containing 30mL / L of methanesulfonic acid and 100g / L of hydrogen peroxide for microetching treatment at a temperature of 25°C for 2 minutes. After micro-etching treatment, the surface of the silver layer is relatively flat and smooth; the micro-etching pore size is relatively uniform, ...

Embodiment 3

[0071] Cleaning: Put the silver-based substrate into a super water tank filled with ultra-pure water, immerse the silver-based substrate, apply slight vibration at room temperature, and treat for 10 minutes to remove dust and other impurities on the surface of the silver-based substrate. Then put the product into a mixed solution of sodium dodecylsulfonate and 30g / L sodium hydroxide with a mass fraction of 5% to carry out ultrasonic vibration degreasing treatment; make 80g / L lauryl ammonium chloride and 30mL / L The nitric acid mixture is ultrasonically oscillated for deoxidation treatment.

[0072]Microetching treatment: place the above-mentioned cleaned silver-based substrate in a mixed solution containing 30mL / L of methanesulfonic acid and 100g / L of potassium permanganate for microetching treatment at a temperature of 25°C for 2 minutes , after micro-etching treatment, the surface of the silver layer is flat and smooth; micro-etching pore size uniformity is good, surface roug...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a silver-based circuit board chemically plated with nickel, palladium and gold and a preparation method of the silver-based circuit board. The silver-based circuit board comprises a silver-based substrate, wherein a nickel layer, a palladium layer and a gold layer are sequentially plated on the surface of the silver-based substrate from inside to outside. The preparation method comprises the steps of sequentially carrying out pretreatments of micro etching, acid pickling, pre-pickling, palladium activation and post-pickling on the cleaned silver-based substrate, and then sequentially carrying out chemical nickel plating, chemical palladium plating and chemical gold plating on the pretreated silver-based substrate to obtain the silver-based circuit board with the nickel, palladium and gold plating layers. Compared with the traditional chemical plating of nickel, palladium and gold on a copper-based substrate, the thickness of the nickel, palladium and gold plating layers can be greatly reduced, so that the use content of the metal is saved, and the problem of environmental pollution is avoided; and in addition, the substrate is silver-based, so that the wholecircuit board is higher in electrical conductivity and thermal conductivity, higher in sensitivity, longer in service life, and more excellent in overall performance.

Description

technical field [0001] The invention relates to a silver-based circuit board with electroless nickel-palladium-gold plating and a preparation method thereof, belonging to the technical field of surface treatment technology. Background technique [0002] With the rapid development of the electronics industry, the demand for circuit boards is increasing day by day. However, today's electronic products have gradually developed towards the direction of multi-function, high performance, portability, reliability and low cost. In order to meet the needs of the market and technology, it is not only required that the electronic packaging process must move towards high-density packaging such as system packaging or IC packaging. There is a need for a coating that can meet a variety of packaging processes, so the "universal" reputation of the electroless nickel-palladium-gold surface treatment process is born from this. [0003] The main processes of electroless nickel palladium platin...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C23C18/36C23C18/44C23C18/18
CPCC23C18/1651C23C18/1844C23C18/36C23C18/44
Inventor 肖忠良曾超肖敏之刘青吴道新
Owner 珠海联鼎化工设备有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap