Building adhesive for steel structure and preparation method of building adhesive

A technology for adhesives and steel structures, applied in the direction of monocarboxylate copolymer adhesives, adhesives, adhesive types, etc., can solve the problem of insufficient capacity, high temperature resistance of adhesives, rust prevention, corrosion resistance and use Insufficient service life, less characteristics of building adhesives, etc., to achieve the effect of strong adhesion, improved anti-aging ability, and improved anti-mildew ability

Inactive Publication Date: 2017-10-17
HEFEI ZEJUN ELECTRICAL EQUIP CO LTD
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] But the characteristic of existing building adhesive is few, and ability is insufficient, such as in the patent document that publication number is CN104449536A, discloses a kind of building adhesive for steel structure; Be made by the raw material of following weight number: nanometer oxidation 2-3 parts of zinc, 53-58 parts of polytetrahydrofuran ether glycol, 18-22 parts of isophorone diisocyanate, 2-4 parts of epichlorohydrin, 4-6 parts of dimethylethanolamine, 5 parts of nano-tungsten trioxide -6 parts, 9-12 parts of 6101 epoxy resin, 9-12 parts of carboxyl-terminated liquid polybutadiene rubber, 9-12 parts of nano-silicon carbide, 1.5-2 parts of dodecylbenzenesulfonic acid, 6 parts of zinc isooctanoate -9 parts, boron trifluoride monoethylamine 5-6 parts
The building adhesive for steel structures of the invention has strong adhesive force, good mechanical properties, and can be cured at room temperature, especially the "steel-steel" bonding shear strength and the "steel-concrete" bonding shear strength are high, and have good Excellent toughness and impact resistance, the tensile strength of steel-steel bonding reaches 61.8MPa; but the high temperature resistance, rust resistance, corrosion resistance and service life of the adhesive are insufficient, and it is difficult to meet the needs of building development

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] A kind of building adhesive for steel structure of the present embodiment comprises the following raw materials in parts by weight:

[0026] 15 parts of silicate, 4 parts of starch, 15 parts of fluorosilicone rubber, 70 parts of vinyl acetate resin, 7 parts of ceramic fiber, 12 parts of aluminum powder, 4 parts of titanium dioxide, 3 parts of molybdenum disulfide, 1 part of curing agent, accelerator 2 parts of anti-rust agent, 3 parts of anti-rust agent, 0.5 part of anti-fungal agent, and 0.5 part of anti-aging agent.

[0027] In this embodiment, the length of the ceramic fiber is 0.5 mm, and the diameter is 0.1 mm; the mesh number of the aluminum powder and the titanium dioxide is 120 mesh.

[0028] In this embodiment, the curing agent is a mixture of diaminodiphenylmethane and vinyltriamine, and the weight ratio between the two is 1:3.

[0029] In this embodiment, the accelerator is a mixture of triethanolamine, dibutyltin dilaurate, stannous octoate, cobalt naphthen...

Embodiment 2

[0039] A kind of building adhesive for steel structure of the present embodiment comprises the following raw materials in parts by weight:

[0040] 17 parts of silicate, 5 parts of starch, 16 parts of fluorosilicone rubber, 75 parts of vinyl acetate resin, 8 parts of ceramic fiber, 14 parts of aluminum powder, 5 parts of titanium dioxide, 4 parts of molybdenum disulfide, 1.5 parts of curing agent, accelerator 2.3 parts of antirust agent, 3.5 parts of antirust agent, 0.8 part of antifungal agent, and 0.7 part of antiaging agent.

[0041] In this embodiment, the length of the ceramic fiber is 0.8mm, and the diameter is 0.3mm; the mesh number of the aluminum powder and the titanium dioxide is 120 mesh.

[0042] In this embodiment, the curing agent is a mixture of diaminodiphenylmethane and vinyltriamine, and the weight ratio between the two is 1:3.

[0043] In this embodiment, the accelerator is a mixture of triethanolamine, dibutyltin dilaurate, stannous octoate, cobalt naphthe...

Embodiment 3

[0053] A kind of building adhesive for steel structure of the present embodiment comprises the following raw materials in parts by weight:

[0054] 18 parts of silicate, 6 parts of starch, 17 parts of fluorosilicone rubber, 80 parts of vinyl acetate resin, 9 parts of ceramic fiber, 16 parts of aluminum powder, 6 parts of titanium dioxide, 5 parts of molybdenum disulfide, 2 parts of curing agent, accelerator 3 parts of anti-rust agent, 4 parts of anti-rust agent, 1 part of anti-fungal agent, and 0.8 parts of anti-aging agent.

[0055] In this embodiment, the length of the ceramic fiber is 1 mm, and the diameter is 0.5 mm; the mesh number of the aluminum powder and the titanium dioxide is 120 mesh.

[0056] In this embodiment, the curing agent is a mixture of diaminodiphenylmethane and vinyltriamine, and the weight ratio between the two is 1:3.

[0057] In this embodiment, the accelerator is a mixture of triethanolamine, dibutyltin dilaurate, stannous octoate, cobalt naphthenat...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
diameteraaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a building adhesive for a steel structure and belongs to the technical field of adhesives. The building adhesive comprises the following raw materials in parts by weight: 15-18 parts of silicate, 4-6 parts of starch, 15-17 parts of fluorinated silicone rubber, 70-80 parts of vinyl acetate resin, 7-9 parts of ceramic fiber, 12-16 parts of aluminum powder, 4-6 parts of titanium dioxide, 3-5 parts of molybdenum disulfide, 1-2 parts of a curing agent, 2-3 parts of an accelerant, 3-4 parts of an anti-rusting agent, 0.5-1 part of an anti-mold agent and 0.5-0.8 part of an anti-aging agent. The invention further discloses a preparation method of power equipment protection paint. The building adhesive is good in adhesion property, high in strength, good in rusting resistance, high temperature resistance and corrosion resistance and long in service life.

Description

technical field [0001] The invention relates to the technical field of adhesives, in particular to a building adhesive for steel structures and a preparation method thereof. Background technique [0002] Steel structure is a structure mainly made of steel, which is one of the main types of building structures. Steel is characterized by high strength, light weight, good overall rigidity, and strong deformation ability, so it is especially suitable for building large-span, ultra-high, and ultra-heavy buildings; the material has good homogeneity and isotropy, and is an ideal elastic body , which is most in line with the basic assumptions of general engineering mechanics; the material has good plasticity and toughness, can have large deformation, and can withstand dynamic loads well; the construction period is short; its high degree of industrialization can carry out specialized production with a high degree of mechanization. Steel structures should study high-strength steel to...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J131/04C09J183/08C09J11/04C09J11/06C09J11/08
CPCC09J131/04C08K2003/0812C08K2003/162C08K2003/2241C08K2003/3009C08K2003/3045C08K2201/014C08L2201/08C08L2205/03C09J11/04C09J11/06C09J11/08C08L83/08C08L3/02C08K13/04C08K7/04C08K3/34C08K3/08C08K3/22C08K3/30C08K3/16
Inventor 徐仙峰
Owner HEFEI ZEJUN ELECTRICAL EQUIP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products