Eureka AIR delivers breakthrough ideas for toughest innovation challenges, trusted by R&D personnel around the world.

Jade vein simulated high-intensity low-shrinkage amino moulding plastic particle material and production method

A technology of low amino group and molding particles, applied in the field of plastics, can solve the problems of difficult to effectively improve the quality and output, high dust of finished products, high labor intensity, etc., and achieve the effects of fast curing, low cost and low cost.

Inactive Publication Date: 2015-11-04
陈天云
View PDF0 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This method is labor-intensive, consumes a lot of energy, pollutes the environment, and is harmful to the human body. The finished product has a lot of dust, low density, poor appearance, and it is difficult to effectively improve the quality and output.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] Example 1: Take 240 kg of formaldehyde aqueous solution, 138 kg of urea, 6 kg of melamine, additives (8.8 kg of urotropine, 0.6 kg of oxalic acid, ammonium sulfamate, magnesium oxide, zinc oxide, ammonium chloride, ethanol, 5.7 kg of triethanolamine, ammonia, PPG, T8, sodium naphthalene sulfonate, glycerin, magnesium carbonate, resorcinol, etc., 4 kg of pigments and zinc stearate, 18 kg, etc. are added to the vacuum granulation reactor integrated machine, Choose the general alkali-acid-alkali synthetic resin.

[0013] Add 165 kilograms of wood powder, inorganic short and medium fibers, etc. into the resin solution, vacuum granulation reactor integrated machine, fully stir and mix, stir at high speed for 2 to 5 minutes, then turn to low speed, the reaction temperature of the material is 50-60 Keep the temperature at temperature for 60 minutes, open the vacuum valve to pump water vapor, heat up and stir at low speed for 10-15 minutes, and the material temperature is 60-85°C....

Embodiment 2

[0014] Example 2: Take 300 kilograms of formaldehyde aqueous solution, 150 kilograms of urea, 10 kilograms of melamine, additives (8.8 kilograms of urotropine, 0.6 kilograms of oxalic acid, water, ammonium sulfamate, magnesium oxide, zinc oxide, ammonium chloride, ethanol, 6.4 kg of triethanolamine, ammonia, PPG, T8, sodium naphthalene sulfonate, glycerin, magnesium carbonate, resorcinol, etc., 5 kg of pigments and zinc stearate) 20 kg, etc. are added to the vacuum granulation reactor integrated machine, Choose the general alkali-acid-alkali synthetic resin.

[0015] Put 350 kilograms of wood powder, 150 kilograms of fruit shell powder, and 20 kilograms of calcium oxide, which is mainly bone meal, into the integrated machine for closed production with polymerization, kneading, dispersion, and drying as in Example 1. Environmentally friendly, economical and durable amino molding pellets.

Embodiment 3

[0016] Example 3: Take 180 kilograms of formaldehyde aqueous solution, 110 kilograms of urea, 1 kilogram of melamine, additives (6 kilograms of urotropine, 0.3 kilograms of oxalic acid, water, ammonium sulfamate, magnesium oxide, zinc oxide, ammonium chloride, ethanol, 5.7 kg of triethanolamine, ammonia, PPG, T8, sodium naphthalenesulfonate, glycerin, magnesium carbonate, resorcinol, etc., 3 kg of pigments and zinc stearate) 15 kg, etc. are added to the vacuum granulation reactor integrated machine, Choose the general alkali-acid-alkali synthetic resin.

[0017] The vacuum granulation reactor integrated machine is in the state of stirring, and 28 kilograms of waste cotton, linen, chemical fiber, glass fiber and other fibers, 46 kilograms of waste paper pulp powder, and 33 kilograms of kaolin are sequentially added. The following operations are the same as in Example 1, polymerization, kneading, and dispersion. , Dry and other closed production. The material can be used ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a jade vein simulated high-intensity low-shrinkage amino moulding plastic particle material and a production method. The high-intensity low-shrinkage amino moulding plastic particle material is characterized by being prepared from formaldehyde water solution, urea, melamine, auxiliary agents, sodium hudroxide, filling materials and the like, wherein the filling materials are mixed bodies of wood powder, inorganic and organic medium short fiber, paper pulp plates, waste paper wood pulp, grain and fruit hulls, bone meal, starch and inorganic oxides; the auxiliary agents are urotropine, oxalic acid, water, ammonium sulfamate, magnesium oxide, zinc oxide, ammonium chloride, ethanol, trolamine, ammonia water, PPG, T-8, sodium-naphthalenesulfonate, glycerin, magnesium carbonate, hydroxyphenol, pigment, zinc stearate and the like. The production method of the jade vein simulated high-intensity low-shrinkage amino moulding plastic particle material comprises the following steps that in a resin synthesis stage, a general alkali-acid-alkali method is selected for synthesizing the resin; in an evaporation polycondensation stage, the resin and the filling materials are input into a vacuum granulation reaction kettle, and the sealed production is completed in one step.

Description

technical field [0001] The invention relates to the field of plastics, in particular to the production process of environment-friendly amino molding pellets. Background technique [0002] With the advancement of human civilization, people's awareness of environmental protection is getting stronger and stronger, and their requirements for green and environmental protection are getting higher and higher, and plastics that are close to people's lives have attracted more attention from consumers. Many non-toxic, harmless, non-polluting and degradable new plastic varieties have been widely used in furniture and building materials decoration, daily necessities, handicrafts, tableware and other fields due to their convenient processing and molding, bright colors and low cost. The use of wood flour, sawdust, shavings, plant fibers, husks, shell powder, starch and inorganic oxides to improve thermosetting resins is a type of non-toxic and harmless plastic products. [0003] At prese...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L61/30C08L97/02C08K3/22C08K3/34C08G12/38
Inventor 陈天云
Owner 陈天云
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com