A kind of preparation method of waterborne polyurethane/collagen/hydroxyapatite composite material

A technology of water-based polyurethane and hydroxyapatite, which is applied in prosthesis, tissue regeneration, medical science, etc., can solve problems such as difficult to balance mechanical properties, biological functions and biodegradable properties, lack of osteoinductive activity, and poor plasticity , to achieve the effects of controllable mechanical processability, good biocompatibility and low cost

Active Publication Date: 2021-09-24
QILU UNIV OF TECH
View PDF13 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, in most cases, HAP bioceramics prepared by high temperature have disadvantages such as poor plasticity, brittle texture, and lack of osteoinductive activity, and it is difficult to properly balance mechanical properties, biological functions, and biodegradable properties.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of waterborne polyurethane/collagen/hydroxyapatite composite material
  • A kind of preparation method of waterborne polyurethane/collagen/hydroxyapatite composite material
  • A kind of preparation method of waterborne polyurethane/collagen/hydroxyapatite composite material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0048] Example 1, a method for preparing a water-based polyurethane / collagen / hydroxyapatite composite material, the material is prepared using a glass three-necked flask, equipped with vacuum dehydration, heating and cooling, condensation reflux, constant pressure dripping device, including the following steps :

[0049] (1) Weigh 50 g of polyethylene adipate diol (molecular weight: 2000), vacuum dehydrate at 110°C for 1~2 h, cool down to 60°C, add 45 g of diphenylmethane diisocyanate to react 1 h, be warming up to 82 DEG C, be incubated 1 h and obtain prepolymer;

[0050](2) In step (1), the temperature of the prepolymer was lowered to 60°C, and 5 g of dimethylolpropionic acid was added for chain extension, and reacted for 1 h, and then 8 g of diethylene glycol was added to the system for Chain extension, after reacting for 30 minutes, raise the temperature to 82°C and keep it warm for 2-3 hours until -NCO is close to the theoretical value (detected by di-n-butylamine method...

Embodiment 2

[0055] Embodiment 2, a kind of preparation method of aqueous polyurethane / collagen protein / hydroxyapatite composite material, comprises the following steps:

[0056] (1) Weigh 50 g of polytrimethylene adipate diol (molecular weight 2000), vacuum dehydrate at 105°C for 1~2 h, cool down to 60°C, add 30 g of toluene diisocyanate, react for 1 h, and heat up to 82 ° C, incubated for 1 h to obtain the prepolymer;

[0057] (2) Cool the prepolymer to 60°C in step (1), add 5 g of dimethylolpropionic acid for chain extension, react for 1 h, add 3 g of propylene glycol to the system for chain extension, and react for 30 min, Heat up to 80°C, keep warm for 2-3 hours;

[0058] (3) Cool the product in step (2) to 50°C, add 3.5 g of triethylamine for neutralization, and add an appropriate amount of acetone to adjust the viscosity. After being cooled to room temperature, add 5 DEG C of deionized water 1100r / min and stir for 5 min to obtain an aqueous polyurethane prepolymer emulsion;

[00...

Embodiment 3

[0062] Embodiment 3, a kind of preparation method of aqueous polyurethane / collagen protein / hydroxyapatite composite material, comprises the following steps:

[0063] (1) Weigh 40 g isophorone diisocyanate, 50 g polybutylene adipate diol (molecular weight 2000) after vacuum dehydration, 1~2 drops of dibutyltin dilaurate catalyst, at 65°C Reaction 1 h, be warming up to 80 ℃, insulation 1~2 h obtains prepolymer;

[0064] (2) Add 6 g of dihydroxybutyric acid to the prepolymer in step (1) for chain extension, react at 60°C for 1 h, add 7 g of diethylene glycol to the system for chain extension, and keep warm at 60°C for 1 h , be warming up to 80 DEG C, react 2~3 h;

[0065] (3) Cool the product in step (2) to 50°C, add 4 g of triethylamine for neutralization, and adjust the viscosity with an appropriate amount of acetone. After being cooled to room temperature, add 5 DEG C of deionized water 1200r / min and stir for 5 min to obtain an aqueous polyurethane prepolymer emulsion;

[0...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for preparing a water-based polyurethane / collagen / hydroxyapatite composite material, which comprises the following components in parts by weight: diisocyanate, polyester polyol, chain extender, water-based chain extender, neutralizer, Hydrolyzed Collagen Solution, γ‑Glycidyl Etheroxypropyl Trimethoxysilane (KH560), Calcium Chloride, Disodium Hydrogen Phosphate. In the present invention, polyester-type water-based polyurethane (WPU) prepolymer and biochemical grade gelatin hydrolyzate (GH) are used for emulsion polymerization, and KH560 is further modified by external linking to improve the hydrophobicity of the material and the toughness of the film, so that WPU and GH graft copolymerization compound emulsion (WPU‑g‑GH). The aim is to prepare a nano-HAP composite material with good mechanical properties, structural stability, biocompatibility and degradability, which is expected to become a potential bone scaffold repair material.

Description

technical field [0001] The invention relates to a preparation method of a water-based polyurethane / collagen / hydroxyapatite composite material, belonging to the field of biomedical polymer materials. Background technique [0002] Bone defects are usually caused by congenital diseases, trauma, infection, tumors. The use of autografts and allografts to replace and repair bone defects has been limited due to supply shortages, additional complications, and immune rejection. [0003] Therefore, designing and manufacturing artificial bone repair or substitutes with good mechanical properties, biocompatibility, biodegradability and porous structure by simulating the formation mechanism of natural tissues has become an important research direction in recent years. Bone is essentially a biological composite of inorganic minerals and collagen. Hydroxyapatite (HAP, Ca 10 (PO 4 ) 6 (OH) 2 ) nanocrystals, as an important inorganic mineral in bone tissue, have been widely studied and...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08G18/83C08G18/66C08G18/64C08G18/48C08G18/34C08G18/32C08G18/10C08K3/32A61L27/46A61L27/58
CPCA61L27/46A61L27/58A61L2300/412A61L2430/02C08G18/10C08G18/4238C08G18/6446C08G18/837C08K3/32C08K2003/325C08G18/348C08G18/3206C08G18/64C08L75/06
Inventor 杨茂张敏李彦春祝德义鹿文慧
Owner QILU UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com