One-component transparent waterborne polyurethane emulsion waterproof paint and preparation method thereof

A technology of water-based polyurethane and waterproof coatings, which is applied in coatings and other directions, can solve the problems of small width, poor water resistance and solvent resistance, and needs to be improved in water resistance and solvent resistance, so as to achieve the effect of increasing hardness and improving hydrophobic performance

Inactive Publication Date: 2016-01-20
XIAMEN UNIV
View PDF8 Cites 41 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

CN104293160A has prepared a kind of environment-friendly polyurethane coating, utilizes 2,4-xylene diisocyanate and polytetramethyl glycol to react to prepare aqueous polyurethane liquid, then adds nano-titanium dioxide, nano-silica and defoaming to this system The final environmentally friendly coating is prepared by stirring and mixing additives and film-forming aids. Although polyurethane can improve the anti-pollution and self-cleaning properties by adding inorganic nanoparticles, the dispersion of the particles is poor during the simple physical mixing process, and the coating Poor performance uniformity
CN103614065A Add water-based polyurethane emulsion, multi-functional additives, matting powder and deionized water sequentially under mechanical stirring, and then add surface additives, water-based wax emulsion, preservative and water-based thickener until the paint liquid is evenly prepared after dispersing for a certain period of time A kind of matte clear finish paint, although the product made in the present invention has higher hardness, and drying speed is also faster, but hydrophobic property is relatively poor
[0005] In recent years, due to polyurethane and its unique excellent properties, many people continue to explore and research. In 2013, Shin et al. reported a fluorine-containing waterborne polyurethane-acrylate block copolymer prepared by a solvent-free method (ShinMS , LeeYH, RahmanMM, etal.Synthesis and properties of waterbornefluorinatedpolyurethane-acrylateusingasolvent-/emulsifier-freemethod[J].Polymer,2013,54(18):4873-4882.), but this product is only pure resin polymerization, and the fluorine-containing segment acts as The soft segment exists in polyurethane, and the hardness of the coating film is low, which also makes the mechanical properties of the coating film relatively poor, and the water resistance and solvent resistance are poor.
In 2014, Luo et al. obtained water-based polyurethane through prepolymerization of diisocyanate and diol, emul...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • One-component transparent waterborne polyurethane emulsion waterproof paint and preparation method thereof
  • One-component transparent waterborne polyurethane emulsion waterproof paint and preparation method thereof
  • One-component transparent waterborne polyurethane emulsion waterproof paint and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0059] The one-component transparent water-based polyurethane emulsion waterproof coating of the present invention is prepared from the following raw materials according to mass percentage: 20% of isophorone diisocyanate, 60% of polypropylene glycol, 0.05% of dibutyltin dilaurate, and hydroxyl-terminated polysilicon Oxane 3%, Dimethylolpropionic Acid 3.5%, Hydroxyethyl Acrylate 3.2%, Methylpropylene Glycol 3.8%, Triethylamine 6%, Trimethylolpropane Glycidyl Ether 3.3%, Ammonium Persulfate 0.5%, The solid content is 40-50%.

[0060] In the first step, add isophorone diisocyanate, polypropylene glycol (Mn=2000) and dibutyltin dilaurate into the reaction kettle, stir evenly with a mechanical stirrer, heat up to 75°C for 2 hours, and then dissolve the , Add dimethylolpropionic acid in N-dimethylformamide to the mixed system, heat to 80°C for 3 hours; cool down to 60°C, add methylpropylene glycol and hydroxyethyl acrylate to the system, keep warm to continue the reaction 4h; At th...

Embodiment 2

[0064] The preparation process of the high-transparency water-based polyurethane waterproof coating described in this example is similar to that of the example, the difference is that the raw material ratio of this example is: 30% of isophorone diisocyanate, 50% of polypropylene glycol, and hydroxyl-terminated polysilicon Oxane 6%, Dibutyltin Dilaurate 0.06%, Dimethylolpropionate 3.4%, Hydroxyethyl Acrylate 3.4%, Methylpropylene Glycol 3.8%, Triethylamine 1.4%, Trimethylolpropane Glycidyl Ether 2 %, ammonium persulfate 0.6%, solid content 40-50%.

[0065] The performance test results are shown in Table 1.

Embodiment 3

[0067]The preparation process of the transparent water-based polyurethane waterproof coating described in this example is similar to that of the example, the difference is that the raw material ratio of this example is: 26% of isophorone diisocyanate, 48% of polypropylene glycol, hydroxyl-terminated polysiloxane Alkanes 8%, Dibutyltin Dilaurate 0.04%, Dimethylolpropionic Acid 2%, Hydroxyethyl Acrylate 3%, Methylpropylene Glycol 4%, Triethylamine 4%, Trimethylolpropane Glycidyl Ether 5% , Ammonium persulfate 0.4%, solid content is 40-50%.

[0068] The performance test results are shown in Table 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Diameteraaaaaaaaaa
Particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses one-component transparent waterborne polyurethane emulsion waterproof paint and a preparation method thereof and relates to polyurethane waterproof paint. The waterproof paint comprises a resin phase and a nano-material phase. The preparation method comprises the following steps: diol and a hydrophilic chain extender are dried, and other prepolymerization monomers are dried; diol, diisocyanate, fluorine-containing acrylate monomers and hydroxyl-terminated siloxane after a dehydration process are added to a four-neck flask, the mixture is heated and added with an organic tin initiator for a reaction under the protection of nitrogen, and the mixture is heated and added with dimethylolpropionic acid for continuous reaction; after a reaction system is cooled, the chain extender and acrylate monomers are added for a reaction; after a prepolymer is cooled to the temperature lower than the room temperature, a neutralizer and a cross-linking agent are added; then deionized water is added for emulsification, and mixed liquor A is obtained; a silane coupling agent is dissolved in absolute ethyl alcohol, silica microspheres are added to absolute ethyl alcohol, and mixed liquor B is obtained; the mixed liquor B is added to the mixed liquor A, the mixture is heated, and a radical initiator is added for a reaction; an organic solvent is removed, and the one-component transparent waterborne polyurethane emulsion waterproof paint is obtained.

Description

technical field [0001] The invention relates to a polyurethane waterproof coating, in particular to a one-component transparent water-based polyurethane emulsion waterproof coating and a preparation method thereof. Background technique [0002] With the rapid development of the national economy, the demand for coatings is increasing year by year. At the same time, people pay more and more attention to environmental protection, and the use of solvent-based coatings with a high content of volatile organic compounds is increasingly restricted. Waterborne polyurethane (WPU) is a green and environmentally friendly coating with polyurethane as the base material and water as the dispersion medium. Compared with traditional solvent-based polyurethanes, WPU not only retains the advantages of traditional solvent-based polyurethanes, but also has excellent properties such as non-toxic, non-flammable, and environmentally friendly. It has been widely used in coatings, adhesives, leather...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D175/08C09D151/08C09D7/12C08G18/67C08G18/66C08G18/65C08G18/61C08G18/32C08F283/00
Inventor 刘向阳于芳芳林乃波
Owner XIAMEN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap