39 results about "Deciliters" patented technology

A composite-forming process includes impregnating a reinforcing structure with a curable composition at a temperature of about 10 to about 40° C. The curable composition includes specific amounts of an epoxy resin, a poly(arylene ether), a solvent, and a curing promoter. The poly(arylene ether) includes, on average, about 1.6 to about 2.4 phenolic hydroxy groups per molecule, and it has a polydispersity index less than or equal to 2.2 and an intrinsic viscosity of about 0.03 to about 0.2 deciliter per gram. These characteristics substantially improve the solubility of the poly(arylene ether) in the curable composition and allow the curable composition to be formed and used at or near room temperature. Composites formed by the process and circuit boards including the composites are also described.

A curable composition includes an olefinically unsaturated monomer and a poly(arylene ether) having two polymerizable groups and an intrinsic viscosity of about 0.05 to about 0.30 deciliters per gram. The composition exhibits an improved combination of high flow during molding and high post-cure stiffness and impact strength. The composition is particularly useful for fabricating plastic-packaged electronic devices.

The invention provides thermoplastic starch (TPS), which comprises the following ingredients: 20 to 80 weight parts of starch, 5 to 40 weight parts of biodegradable polyester prepolymers, 0.01 to 10 weight parts of reaction active agents, 0.01 to 10 weight parts of catalytic devitalizing agents, 0.01 to 1.0 weight part of antioxidant and 5 to 50 weight parts of auxiliaries, wherein the molecular weight of the prepolymer is 10,000 to 100,000 Daltons, the viscosity number range is 0.30 to 1.2 deciliters per gram and is measured through a Ubbclohde viscosity method, the melting point range is 60to 180 DEG C, and the end reaction group content is 1.0 to 20.0 meq / Kg and is measured by an end group titration method. The invention also provides a biodegradable polyester / starch composite material containing the thermoplastic starch and a preparation method thereof.

This invention relates to a blend comprising(a) about 2% to about 98% by weight of at least one ester of cellulose comprising an alkanoyl chain having from about 1 to about 10 carbon atoms, and having at a D.S. of about 2.3 to about 3.0, and an inherent viscosity of about 0.2 to about 3.0 deciliters / gram as measured at a temperature of 25° C. for a 0.5 g sample in 100 ml of a 60 / 40 parts by weight solution of phenol / tetrachloroethane, and(b) about 98% to about 2% by weight of at least one ester of cellulose comprising an alkanoyl chain having from about 1 to about 10 carbon atoms, and having a D.S. of about 1.5 to about 2.2, and an inherent viscosity of about 0.2 to about 3.0 deciliters / gram as measured at a temperature of 25° C. for a 0.5 g sample in 100 ml of a 60 / 40 parts by weight solution of phenol / tetrachloroethane, said percentages being based on the weight of component (a) plus component (b).

A composite-forming process includes impregnating a reinforcing structure with a curable composition at a temperature of about 10 to about 40° C. The curable composition includes specific amounts of an epoxy resin, a poly(arylene ether), a solvent, and a curing promoter. The poly(arylene ether) includes, on average, about 1.6 to about 2.4 phenolic hydroxy groups per molecule, and it has a polydispersity index less than or equal to 2.2 and an intrinsic viscosity of about 0.03 to about 0.2 deciliter per gram. These characteristics substantially improve the solubility of the poly(arylene ether) in the curable composition and allow the curable composition to be formed and used at or near room temperature. Composites formed by the process and circuit boards including the composites are also described.

Provided is a production process for polyarylene sulfide having a high molecular weight and an excellent heat stability. It is a production process for polyarylene sulfide by reacting a dihalogenoaromatic compound with metal sulfide in a polar solvent, wherein all or a part of water required for the reaction is added on a condition that the reaction system is 100° C. or higher, whereby obtained is polyarylene sulfide which is reduced in an intrinsic viscosity [eta] by 0.05 deciliter / g or less at 206° C. when added to an N-methyl-2-pyrrolidone solvent is the polyarylene sulfide of an amount equivalent to the solvent and it is maintained at 265° C. for 8 hours.

A curable composition includes an epoxy resin and a bifunctional poly(arylene ether) having an intrinsic viscosity of about 0.03 to about 0.2 deciliter per gram. After curing, the composition exhibits markedly improved impact strength relative to a corresponding composition prepared from monofunctional poly(arylene ether).

A syndiotactic polystyrene blend comprises syndiotactic polystyrene and poly(arylene ether) wherein the poly(arylene ether) has an intrinsic viscosity less than about 0.25 deciliters per gram (dl / g) when measured in chloroform at 25° C.

A varnish composition for producing an electrically insulative thermoset coating is disclosed. The varnish composition includes a functionalized poly(phenylene ether) having at least one aliphatic unsaturated group and exhibiting an intrinsic viscosity in the range of about 0.06 to about 0.25 deciliter per gram, measured in chloroform at 25° C. The varnish composition further includes an unsaturated polyester resin or vinyl ester resin, a reactive liquid monomer, and a compatibilizing agent. When cured, the polymers and reactive liquid monomer form an electrically insulative thermoset.

A method having clinically sufficient degree of diagnostic accuracy for detecting the presence of coronary artery disease in a human patient from the general population and for distinguishing between the stages of the disease in that patient is disclosed. The stages are, first, the non-acute stage, which is either asymptomatic coronary artery disease or stable angina, second, the acute stage known as unstable angina, and, third, the acute stage known as acute myocardial infarction. The diseased state (as opposed to the non-diseased state) is indicated by the clinically significant presence of a first marker in a sample from the patient. The presence of one of the two acute stages, unstable angina or acute myocardial infarction, is indicated by the clinically significant presence of a second marker in a sample from the patient. The presence of the more severe acute stage known as acute myocardial infarction is indicated by the clinically significant presence of a third marker in a sample from the patient. Preferably the first marker comprises OxLDL, the second marker comprises MDA-modified LDL, and the third marker is a troponin. Preferably the OxLDL and MDA-modified LDL are detected using monoclonal antibodies that can detect the presence of those markers in undiluted human plasma at concentrations as low as 0.02 milligrams / deciliter.

The invention discloses double-layer full-orientation and direct-interconnection overpass, the overpass is made up of bridge approach, deciliter tilt hole, cross bridge and inner arc curved road, the deciliter tilt hole and curved road are double-layer structure with upper and subjacent layer, each bridge approach is a mutual double bridge which contain a long and a short bridge, which two are connected to the outer end of upper and subjacent layer of the hole, the two sides of each layer in deciliter tilt holes are connected through curved road bridge, the centre part of the each hole is connected to cross bridge, the cross bridge are straight bridges which are orthogonal, the cross bridge is bidirectional one-way bridge, the two ends of it are connected with the upper and subjacent layer of the hole. The overpass can realize full-orientation and direct-interconnection with small area and cost.

The invention discloses a method for producing rayon by using PTT and PET. Firstly, the rayon is prepared from ,by mass, 41-55 parts of PTT raw materials and 41-55 parts of PET raw materials, PET slices with low viscosity is selected as the PET raw materials, and the viscosity of the PET slices is not higher than 0.53 deciliter per gram; the PTT raw materials make the viscosity of PTT slices higher than 1.18 deciliters per gram through drum tackifier, so that the viscosity difference of the PTT raw materials and PET raw materials is increased as much as possible, and then the rayon is formed by melting, spinning and stretching. The method for producing the rayon by using the PTT and the PET makes fibers exert maximum elastic performance, and improves spinnability.

A process for preparing a redistributed poly(phenylene ether), comprising reacting a poly(phenylene ether) in a reactive diluent monomer with a polyhydric phenol in the presence of a redistribution catalyst to form a composition comprising a redistributed poly(phenylene ether) in the reactive monomer diluent. The redistributed poly(phenylene ether) exhibits an intrinsic viscosity in the range of about 0.06 deciliters per gram to about 0.25 deciliters per gram, measured in chloroform at 25° C. The redistributed poly(phenylene ether) can be functionalized and admixed with unsaturated resin such as an unsaturated polyester resin or vinyl ester resin to obtain a varnish composition that, when cured, can form an electrically insulative thermoset.

A composition is disclosed, comprising, based on the total weight of the composition, a combination of from 44 to 80 weight percent of a thermoplastic poly(butylene terephthalate); from 20 to 50 weight percent of a thermoplastic poly(ethylene terephthalate) having an intrinsic viscosity of 0.5 to 0.8 deciliters per gram, measured in a 60:40 by weight phenol / 1,1,2,2-tetrachloroethane mixture at 23° C. using a relative viscometer operating with a closed loop system, which measures the solvent and sample viscosity simultaneously; from 5 to less than 20 weight percent of a talc filler having an average largest dimension of less than 0.9 micrometers, a median particle size of less than 0.9 micrometers, or both; and from 0.1 to 0.5 weight percent of a mold release agent. The compositions are useful in the manufacture of lighting articles, which can be directly metallized without the inclusion of a base coat.

A pharmaceutical composition for therapeutic administration of pyrophosphate for phosphate repletion may be in either liquid or solid form and may be usable as or usable for preparing a hemodialysis or peritoneal dialysis solution containing a pyrophosphate compound present in an amount that provides a concentration in the dialysis solution equivalent to an inorganic phosphorus concentration of at least 0.5 mg per deciliter.

The present invention provides a composition suitable for use in plumbing applications, the composition comprising: an ultra-high molecular weight ethylene-based polymer having an inherent viscosity of 5 to 50 deciliters / gram; a polyethylene resin comprising a first molecular weight ethylene-based polymer a polymer component and a second molecular weight ethylene-based polymer component, wherein the polyethylene resin has a density of 0.930 to 0.960 g / cc; a thermoplastic polyolefin elastomer has a density of 0.850 to 0.910 g / cc; and optionally of fluoropolymers.