The invention belongs to the technical field of
pitch-wood-
wool plate production processes and provides a
pitch-wood-
wool plate production process. The
pitch-wood-
wool plate production process comprises the following steps of
material selection, wherein
firewood with the
diameter greater than or equal to 30 mm and the breakage percentage and the worm damage percentage smaller than or equal to 15% is selected, and impurities in the
firewood are removed;
slicing, wherein the selected
firewood is sequentially sent into a
slicing machine to be machined into wood pieces; wool
grinding, wherein the wood pieces are sent into a hot-
grinding machine to be machined into wood fibers; impregnation, wherein the wood fibers are added into a pitch impregnation device, pitch is quantitatively supplied by the pitch impregnation device, stirring and mixing are conducted, the temperature is maintained to be 150-170 DEG C, the pressure intensity is maintained to be 0.75-0.9 MPa till the wood fibers and the pitch are fused and impregnated, and the
mass ratio of the wood fibers to the pitch is 10: (2.8-3.2); and shaping, wherein pitch-wood fibers which are impregnated completely are pushed to a flat laying
machine, after a preliminary plate shape is formed, the pitch-wood fibers are sent to a cold press for shaping and then sent to a
hot press for
drying, a semi-finished pitch-wood-wool plate is formed, and after
cutting, packaging and maintenance are completed, the finished product is obtained. By means of the pitch-wood-wool plate production process, the technical problem that in the prior art, pitch-wood-wool plates are easy to age, and in the use process, the pitch-wood-wool plates go bad easily are solved.