The invention discloses a Cr2Nb phase containing CuCr contact material preparing method. The Cr2Nb phase containing CuCr contact material preparing method comprises the following steps that S1, burdening is conducted, and raw materials are matched according to the proportion; S2, vacuum induction smelting is conducted, prepared raw materials are arranged in a ceramic crucible, under vacuum conditions, gradient heating is conducted, and the raw materials are melted; S3, casting cooling is conducted, when the raw materials are completely melted, components are uniform under the action of electromagnetic stirring, molten liquid in the ceramic crucible is poured into a water cooling die, and cooling and furnace discharging are conducted; S4, hot forging deformation and heat treatment are conducted, the hot forging technology is adopted for deforming a cast ingot to the needed size, and then heat treatment is conducted; and S5, machining is conducted, and machining equipment is adopted formachining the cast ingot into the needed contact shape according to a drawing. By means of the Cr2Nb phase containing CuCr contact material preparing method, the strength and the hardness of a contactcan be effectively improved, meanwhile, the high-temperature-resisting performance of the material is greatly improved, the contact is better resistant to ablation and high-temperature deformation, and meanwhile the service life of the contact is greatly prolonged.