The invention proposes a Buddha-Jumping-Over-The-Wall vessel formula and a production process. The Buddha-Jumping-Over-The-Wall vessel formula consists of: 15 to 20 percent of raw illite ore, 45 to 55percent of illite china clay, 10 to 15 percent of kaolin, 10 to 16 percent of lithium feldspar, 5 to 10 percent of potassium sodium feldspar, 1 to 5 percent of calcined talc and 1 to 3 percent of dolomite. The production steps include batching, ball milling, blowing, two times of passage through 100-mesh screen, two times of iron removal by high magnetism, aging, pugging, shaping, glazing and firing. A Buddha-Jumping-Over-The-Wall vessel produced by the formula provided by the invention can prolong the time of food preservation to a certain degree and keep the original taste of food, a rolling method can be adopted for shaping, and compared with the conventional slurry injection method, the invention can reduce 60 percent of manpower, thus reducing the manpower resource cost; moreover, the firing temperature is decreased by 100 DEG C in comparison with the firing temperature of the conventional Buddha-Jumping-Over-The-Wall vessel, so the invention has the effect of energy saving and consumption reduction; after firing, the strength of the Buddha-Jumping-Over-The-Wall vessel is three times the strength of the ordinary Buddha-Jumping-Over-The-Wall vessel, consequently, loss caused by impact in the process of handling is reduced, and the cost of food packaging is further reduced.