The invention discloses black matte granular
glaze, which is mixed
powder containing 0.3-0.5% of million-hole
sieve residues and comprises the following components in percentage by weight: 52%-58% of SiO2, 17.5%-21% of Al2O3, 3.4%-4% of K2O, 1%-1.3% of Na2O, 2%-5% of CaO, 0.5%-1.5% of MgO, 8.5%-11% of BaO and 8.5%-11% of
cobalt black. The preparation method of the black matte granular
glaze comprises the steps of S1, weighing the components according to the formula, adding water, and
grinding until the million-hole
sieve residue of the
glaze water is 0.3-0.5% and the
specific gravity of the water glaze is 1.65-1.68; S2,
coating the surface of a biscuit firing
green body with the glaze water in a glaze spraying
glazing mode, wherein fine point atomization is adopted as a glaze spraying method, and the thickness of a glaze layer is controlled to be 1-1.5 mm; and S3, putting the biscuit firing
green body subjected to glaze spraying into a
kiln, heating to 1230-1250 DEG C,
sintering for 8-12 hours, slowly cooling after
sintering, and discharging from the
kiln to prepare the black matte granular glaze which has the advantages of stable glaze color, high yield, concave-convex glaze surface, stereoscopic impression and the like.