The invention relates to a method for manufacturing a natural-like stone ceramic tile with clear color and luster and boundary. The ceramic tile comprises the following main raw materials in percentage by weight: 10 to 15 percent of low-temperature porcelain powder, 10 to 20 percent of medium-temperature porcelain sand soil, 9 to 18 percent of high-temperature porcelain sand, 10 to 15 percent of washed black mud, 10 to 15 percent of albite powder, 5 to 10 percent of alumina porcelain sand, 10 to 20 percent of sodium porcelain sand, 5 to 18 percent of ball clay, 0.5 to 1 percent of liquefaclent and 0.5 to 1.5 percent of pigment; a process flow of the manufacturing method comprises : material selection, material burdening, ball milling, toning, pulverization, cloth pressing, drying, sintering, polishing, sorting, packaging and warehousing; a sprayed micron antifouling coating process is added between a cloth pressing process and a drying process; the cloth pressing process comprises: powder crushing, full automatic computer-controlled vertical blanking, dropping of line micropowder cloth in a mould, distribution of a base material, and pressing and molding; slurry comprises the following components in percentage by moisture mass: 34 to 36 percent of base material and 32 to 34 percent of ice-thoroughly material; and powder (the fineness is about 250-mesh sieve ) comprises the following components in percentage by weight: 0.8 to 1.0 percent of base material and 0 percent of ice-thoroughly material.