The invention provides a method for producing organic-silicone-modified hydrophilic abnormity polyester fibers. In the invention, organic-silicone-modified hydrophilic polyester chips are prepared, andpolyester fiber producing technology is applied, the spinning temperature is from 265 DEG C. to 288 DEG C., and the draft multiple is from 3.5 to 3.8 times. The produced organic-silicone-modified hydrophilic abnormity polyester fiber can enhance the capillary action by fiber section heteromorphosis, so that the fabrics generates the wicking function because of capillary channels on the fibers or among the fibers so as to have drying and moisture transmitting property. Because modified polyester fiber fabrics have the advantages of favorable moisture absorption performance and comfortable wearing feeling, thereby overcoming the defects of natural fiber that clothes cling to the body and cause people to feel wet and cold when swear amount of people is comparatively large. The organic-silicone-modified hydrophilic abnormity polyester fiber can be used for pure spinning and blend spinning or interweaving with cotton, wool, silk, flax and other chemical fibers and synthetic fibers. The organic-silicone-modified hydrophilic abnormity polyester fiber can be used for mechanical weaving and knitting, and is mainly used in the aspects of gym suits, sportswear, underwear, coats, socks, gloves, bras, protective film, caps, towels and the like. The fabrics made of the organic-silicone-modified hydrophilic abnormity polyester fibers enable people to feel dry and comfortable.