The invention discloses a fireproof flame-retardant type coating for a glass door. The fireproof flame-retardant type coating is characterized by being prepared from the raw materials in parts by weight: 34-38 parts of water-based amino resin FY737, 8-12 parts of modified styrene-acrylic emulsion, 20-24 parts of polytetrafluoroethylene emulsion, 0.2-0.4 part of organic silicon defoamer, 1-3 parts of di(propylene glycol) methyl ether acetate, 0.3-0.6 part of alkylol amine dipyrophosphate hydroxyacetate titanate, 0.3-0.5 part of leveling agent BYK-56, 0.3-0.7 part of cocoanut fatty acid diethanolamide, 0.5-1.0 part of D-trehalose, 0.3-0.6 part of tetraethylene glycol monolaurate, 0.4-0.7 part of mica powder, 0.6-1.2 parts of cyanuric acid spiro phosphate, 0.2-0.5 part of carboxymethyl cellulose, 10-13 parts of silicon oxide sol, 0.4-0.6 part of expanded vermiculite powder, 1-3 parts of pigments, and 10-15 parts of deionized water. The added modified styrene-acrylic emulsion has bactericide, dustproof and anti-static functions, and added cyanuric acid spiro phosphate has expanded and flame-retardant effects, so that the expansion of fire disasters can be prevented, and the loss of life and property can be reduced; and the film formed by the water-based coating is flat and smooth, and proper in hardness, and the fireproof flame-retardant type coating also has excellent weather resistance, water resistance, acid resistance and the like, and is safe and environment-friendly, and harmless to an environment and human.